Transition metal hydroxides (M‐OH) and their heterostructures (X|M‐OH, where X can be a metal, metal oxide, metal chalcogenide, metal phosphide, etc.) have recently emerged as highly active electrocatalysts for hydrogen evolution reaction (HER) of alkaline water electrolysis. Lattice hydroxide anions in metal hydroxides are primarily responsible for observing such an enhanced HER activity in alkali that facilitate water dissociation and assist the first step, the hydrogen adsorption. Unfortunately, their poor electronic conductivity had been an issue of concern that significantly lowered its activity. Interesting advancements were made when heterostructured hydroxide materials with a metallic and or a semiconducting phase were found to overcome this pitfall. However, in the midst of recently evolving metal chalcogenide and phosphide based HER catalysts, significant developments made in the field of metal hydroxides and their heterostructures catalysed alkaline HER and their superiority have unfortunately been given negligible attention. This review, unlike others, begins with the question of why alkaline HER is difficult and will take the reader through evaluation perspectives, trends in metals hydroxides and their heterostructures catalysed HER, an understanding of how alkaline HER works on different interfaces, what must be the research directions of this field in near future, and eventually summarizes why metal hydroxides and their heterostructures are inevitable for energy‐efficient alkaline HER.

Over the years, significant advances have been made to boost the efficiency of water splitting by carefully designing economic electrocatalysts with augmented conductivity, more accessible active sites, and high intrinsic activity in laboratory test conditions. However, it remains a challenge to develop earth‐abundant catalysts that can satisfy the demands of practical water electrolysis, that is, outstanding all‐pH electrolyte capacity, direct seawater splitting ability, exceptional performance for overall water splitting, superior large‐current‐density activity, and robust long‐term durability. In this context, considering the features of increased active species loading, rapid charge, and mass transfer, a strong affinity between catalytic components and substrates, easily‐controlled wettability, as well as, enhanced bifunctional performance, the self‐supported electrocatalysts are presently projected to be the most suitable contenders for practical massive scale hydrogen generation. In this review, a comprehensive introduction to the design and fabrication of self‐supported electrocatalysts with an emphasis on the design of deposited nanostructured catalysts, the selection of self‐supported substrates, and various fabrication methods are provided. Thereafter, the recent development of promising self‐supported electrocatalysts for practical applications is reviewed from the aforementioned aspects. Finally, a brief conclusion is delivered and the challenges and perspectives relating to promotion of self‐supported electrocatalysts for sustainable large‐scale production of hydrogen are discussed.

In this analysis, we show that direct seawater splitting with or without additives faces significant challenges and bears almost no advantage with respect to the costs and energy demands to purify water prior to water electrolysis.