The building sector greatly contributes to energy consumption and Greenhouse Gas emissions, relating to the whole building life cycle. Boasting a huge building heritage of historical and architectural value, Europe faces challenging retrofit perspectives, as the potential for high energy efficiency has to be exploited while preserving the buildings’ original characteristics. The present work aims to feature the influence of a passive strategy on a heritage building in a mild climate. As historical its façade cannot be modified, its large glazing areas involve multiple issues, such as an increase in the heating ($Q_H)$ and cooling ($Q_C$) energy demands and the risk of thermal discomfort. Thus, window replacement was proposed for retrofitting. A dynamic simulation model in TRNSYS was validated with experimental data collected by the continuous monitoring of walls of different thicknesses and orientations. Solutions from replacement with Double Glazing Units (DGUs) with improved thermal insulation, to internal shading activation were applied. All configurations were compared in terms of $Q_H$, $Q_C$, thermal performance of the building and user comfort (Fanger). Low-e DGU enabled the saving of up to 14% of the annual energy demand, and shading also offered good results in summer, reducing $Q_C$ by 19%. In summer, DGU involved a maximum PPD reduction of 10 units.

This study aims to investigate the thermo-acoustic and hygrothermal properties of innovative panels made of leather waste produced by a bag factory from a circular economy perspective. Their performance was compared with other residual-based insulation panels. The leather scraps were chipped and three boards were fabricated by means of a mold with different compositions, adding adhesive glue. In order to improve the sustainability aspects, a sample was assembled by using a water-based polyurethane glue, in addition to the two panels with vinyl glue. Panels were tested for thermal, acoustic, and hygrothermal performance. Thermal conductivity values in the range of 0.064–0.078 W/mK at 10 °C were measured depending on the composition and the adhesive. A slight thermal performance deterioration occurs when using the natural water-based glue. The samples were characterized by good performance both in terms of sound absorption coefficient (Noise Reduction Coefficient NRC = 0.21–0.28) and Transmission Loss, up to 59 dB values. Water vapor resistance factor values in the 35–48 range were obtained, close to the values of standard materials, such as expanded polystyrene and polyurethane.

Due to its excellent properties, monolithic silica aerogel is a promising material for innovative glazing systems. Since glazing systems are exposed to deteriorating agents during building service life, it is essential to investigate the long-term performance of aerogel. In the present paper, several 12.7 mm-thick silica aerogel monoliths produced by a rapid supercritical extraction method were tested, including both hydrophilic and hydrophobic samples. After fabrication and characterization of hydrophobicity, porosity, optical and acoustic properties, and color rendering, the samples were artificially aged by combining temperature and solar radiation effects in an experimental device specifically developed at the University of Perugia. The length of the experimental campaign was determined using acceleration factors (AFs). Temperature AF was evaluated according to the Arrhenius law using thermogravimetric analysis to estimate the aerogel activation energy. A natural service life of 12 years was achieved in about 4 months, and the samples’ properties were retested. Contact angle tests supported by FT-IR analysis showed loss of hydrophobicity after aging. Visible transmittance values in the 0.67–0.37 range were obtained for hydrophilic and hydrophobic samples, respectively. The aging process involved optical parameter reduction of only 0.02–0.05. There was also a slight loss in acoustic performance (noise reduction coefficient (NRC) = 0.21–0.25 before aging and NRC = 0.18–0.22 after aging). For hydrophobic panes, color shift values in the 10.2–59.1 and 8.4–60.7 ranges were obtained before and after aging, respectively. The presence of aerogel, regardless of hydrophobicity, results in a deterioration in light-green and azure tones. Hydrophobic samples had lower color rendering performance than hydrophilic aerogel, but this did not worsen after the aging process. This paper makes a significant contribution to the progressive deterioration assessment of aerogel monoliths for applications in sustainable buildings.