This study explored the feasibility of the carbon-free smelting of ferrochrome (FeCr) using a complex reducing agent—ferroaluminosilicalcium alloy (FeAlSiCa)—produced from industrial waste and ferrosilicochrome (FeSiCr) dust. Laboratory-scale smelting experiments were conducted with Cr concentrate and the addition of FeAlSiCa and FeSiCr dust under four different reducing agent contents: (1) 10% deficiency, (2) stoichiometric amount, (3) 10% excess, and (4) 20% excess. It was found that with a 10% excess, a nearly complete reduction of Cr₂O₃ was achieved (residual content in slag ≤ 0.9%), resulting in the formation of low-carbon FeCr (LC FeCr) with a high nitrogen content (up to 2.6%). Based on a thermodynamic analysis of the reduction reactions, the high reactivity of the FeAlSiCa and FeSiCr components (Ca, Al, and Si) at 1500 °C was confirmed. These reactions were exothermic, which demonstrates the energy efficiency of using these ferroalloys as reducing agents in FeCr smelting. The resulting slag is structurally stable and does not disintegrate over time, making it a promising candidate for potential reuse as a secondary raw material. The results demonstrate the promise of the proposed technology for both reducing the carbon footprint of ferroalloy production and lowering the cost of the metallothermic production of LC FeCr.

The article presents the results of a study on the production of a complex chromium–manganese–silicon-containing ferroalloy in a large-scale laboratory ore-thermal furnace using man-made waste—chromium-containing aspiration dust obtained during smelting of high-carbon ferrochrome, fines (−5 mm) of iron–manganese ore currently stored in landfills, and finely dispersed coal sludge formed during enrichment. A single-stage technology for the production of a new complex chromium–manganese–silicon-containing ferroalloy by carbothermal reduction is proposed. A metallurgical assessment of the initial charge materials was carried out by the X-ray diffraction (XRD) phase analysis, and metal samples of the obtained ferroalloy were studied by scanning electron microscopy (SEM) in combination with energy dispersive spectroscopy (EDS). The resulting ferroalloy has a complex microstructure with a predominance of carbide and intermetallic phases. A high degree of extraction of chromium (up to 80%), manganese (up to 75%), and silicon (up to 35%) was recorded. The average chemical composition of the obtained ferroalloy, wt.%: Cr—37.41; Mn—17.31; Si—11.84; C—3.81; P—0.14; S—0.02. The slag formed during the smelting of the ferroalloy has satisfactory technological properties: it is characterized by good fluidity, and it actively exits the furnace by gravity. Entanglement of metal kings in the slag is not observed. The results obtained confirm the technological feasibility of the utilization of technogenic raw materials for the production of complex ferroalloys of the FeCrMnSi type.

This study investigates the use of the complex reductant FeAlSiCa as an alternative to the conventional FeSiCr in the EAF smelting of FeCr. The smelting process using FeAlSiCa is characterized by a stable furnace operation, active discharge of metal and slag, and effective phase separation. It was found that a 20% excess of FeAlSiCa over the stoichiometric requirement leads to a sharp increase in Si content in the FeCr alloy, with approximately 85% Cr recovery into the metal. A stoichiometric amount of FeAlSiCa results in a metal with 1.5–1.6% Si content and about 80% Cr recovery. A comparable Cr recovery using FeSiCr was achieved only when applying a 20% excess of that reductant. The use of FeAlSiCa also holds promise for technological sustainability due to its low production cost and the utilization of waste materials during its synthesis. The resulting slags are solid and rock-like and show no signs of disintegration after storage for more than 45 days.

The article presents the results of comprehensive thermodynamic modeling and laboratory tests conducted for smelting a complex ferroalloy of silicon, manganese, and chromium (Fe-Si-Mn-Cr) from chromium, medium-grade manganese ores, and high-ash coals from Kazakhstan. Thermodynamic analysis was performed using HSC Chemistry software to model the Fe-Si-Mn-Cr smelting process over a temperature range of 900 °C–1800 °C. This analysis involved six actual charge compositions with solid reductant (C_solid) consumption ranging from 5 to 20 kg per 100 kg of Cr and Mn ore mixture. The mechanism of the combined carbothermic reduction of Cr, Mn, Si, and Fe was investigated using the Cr-Si-Al-Ca-Mn-Mg-O-C system. According to thermodynamic data, the optimal consumption of Csolid per 100 kg of ore mixture is 17 kg, and the optimal temperature range for smelting ferroalloys is between 1600 and 1700 °C. Laboratory tests were conducted in a high-temperature Tamman furnace at 1700 °C, resulting in experimental samples of the new complex ferroalloy with an average composition of 14.85% Fe, 14.05% Si, 7.55% Mn, 57.54% Cr, and 6.01% C, with P < 0.03% and S < 0.02%. The phase composition included (Cr, Fe, Mn)₃Si and carbides Cr₂₃C₆ and (Fe, Mn)₃C. The resulting alloy is suitable for alloying high-carbon and tool steels.

Experiments were conducted to pilot the initial reduction in chromium raw materials using the innovative Hoganas technology in a tunnel furnace. To simulate the process, a gas-fired bogie hearth furnace was employed. Technological containers made of silicon carbide crucibles were utilized. Sixteen different combinations of ore and coal mixtures were employed for the initial reduction process. Their total mass was more than 20 tons. Their heat treatment was performed at different temperatures and durations. During the pilot tests, the possibility of achieving chromium metallization was confirmed. Thus, it explains the application of a pre-reduction instead of the sintering or charge heating before the ferrochromium melting, i.e., the power consumption is minimized during the final remelting of the product in DC furnaces. The pilot melting of three batches of the pre-reduced chromium raw materials with various chromium metallization degrees has been tested in the ore-smelting furnace at Zh. Abishev Chemical–Metallurgical Institute (Karaganda). The capacity was 0.2 MVA. To evaluate the technical and economic efficiency of remelting pre-reduced chromium raw materials in commercial DC furnaces, a specific batch of primary ingredients for producing high-carbon ferrochromium, including chromite ore, coke, and quartz flux, was successfully melted in a segregated phase. As a result of the study, it was found that the specific energy consumption for melting high-carbon ferrochromium in the pilot furnace depends on the chromium metallization degree. The researchers tested a range of chromium metallization degrees from 0 to 65% and determined the corresponding specific energy consumption for each degree. Using the data obtained from the study, the researchers were able to assess the melting indexes of high-carbon ferrochromium in a larger 72 MW furnace. They found that by using a pre-reduced product with a chromium metallization degree of 65%, it was possible to reduce the specific energy consumption by half, to around 3.4 MW·h per ton of chromium. Overall, this study highlights the importance of considering the chromium metallization degree when determining the specific energy consumption for melting high-carbon ferrochromium. By optimizing the metallization degree, significant energy savings can be achieved, leading to more efficient and sustainable production processes.

This study investigates the production of chromium–manganese ligature by a metallothermic process using complex silicon–aluminum reducing agents. Low-grade chromium and iron–manganese ores from the Kempirsai and Kerege-Tas deposits in Kazakhstan were used as raw materials, while the reducing agents included alumosilicomanganese alloy (AlSiMn) and ferrosilicoaluminum (FeSiAl). Thermodynamic calculations were performed with HSC Chemistry 10 at 1400–1800 °C and reducing agent dosages of 10–100 kg per 100 kg of ore charge. Crucible smelting experiments were then carried out in a Tamman furnace, followed by large-scale laboratory trials in a 100 kVA refining electric furnace to verify reproducibility, with a total of 14 runs. The chemical composition of the ligatures varied depending on the reductant: with AlSiMn the alloy contained Fe—23.14%, Cr—53.74%, Mn—20.03%, and Si—3.06%; with FeSiAl, it contained Fe—42.01%, Cr—25.74%, Mn—27.15%, and Si—5.05%; and with FeSiCr dust, it contained Fe—34.45%, Cr—21.45%, Mn—39.82%, and Si—4.24%. X-ray diffraction (XRD) and scanning electron microscopy (SEM) analyses confirmed the presence of α-(Fe,Cr,Mn), FeSi, and Cr₅Si₃ phases. The results demonstrate the efficiency of complex silicon–aluminum reducing agents and the ability to regulate the composition of chromium–manganese ligatures by the selected reductant.