This case study was conducted to quantify the effects of urban greenspace patterns on particle matter (PM) concentration in Zhengzhou, China by using redundancy and variation partitioning analysis. Nine air-quality monitoring stations (AQMS) were selected as the central points. Six distances of 1 km, 2 km, 3 km, 4 km, 5 km, and 6 km were selected as the side lengths of the squares with each AQMS serving as the central point, respectively. We found: (1) the fine size of PM (PM_2.5) and coarse size of PM (PM₁₀) among four seasons showed significant differences; during winter, the concentration of PM_2.5 and PM₁₀ were both highest, and PM_2.5 and PM₁₀ concentration in summer were lowest. (2) To effectively reduce the PM_2.5 pollution, the percentage of greenspace, the differences in areas among greenspace patches, and the edge complexity of greenspace patches should be increased at distances of 2 km and 3 km. To effectively reduce PM₁₀, the percentage of greenspace at a distance of 4 km, the edge density at distances of 2 km and 4 km, and the average area of greenspace patches at a distance of 1 km should be increased. (3) Greenspace pattern significantly affected PM_2.5 at a distance of 3 km, and PM₁₀ at a distance of 4 km. From shorter distance to longer distance, the proportion of variance explained by greenspace showed a decline–increase–decline–increase trend for PM_2.5, and a decline–increase–decline trend for PM₁₀. At shorter distances, the composition of greenspace was more effective in reducing the PM pollution, and the configuration of greenspace played a more important role at longer distances. The results should lead to specific guidelines for more cost-effective and environmentally sound greenspace planning.

To develop a lower-cost, excellent performance, and environmentally friendly phe-nol-formaldehyde (PF) resin, soybean meal was used to modify PF resin, and soybean meal-phenol-formaldehyde (SMPF) resins were prepared. Their physicochemical properties and curing performance were investigated, showing that SMPF resins have higher curing tempera-tures than PF resin. The Fourier transform infrared spectroscopy (FTIR) results indicated that the cross-linking reaction occurred between the amino groups of soybean protein and the hy-droxymethyl phenol. Moreover, with the addition of soybean meal, the viscosity of SMPF in-creased while the gel time decreased. It is worth mentioning that SMPF-2 resin has favorable viscosity, short gel time, low curing temperature (135.78 °C), and high water resistance and bonding strength (1.01 MPa). Finally, all the plywoods bonded with SMPF resins have good water resistance and bonding strength, which could meet the Standard (GB/T 17657-2013, type I) for plywood. The optimized SMPF resins showed the potential application to replace part of PF resin in the wood industry.