An attempt at the treatment of the waste fiber (WF) from the wind turbine blade (WTB) was made through the modifier of dopamine hydrochloride and the compound modifier of dopamine hydrochloride and 2,5-dihydroxy terephthalic acid or 3,4-dihydroxy cinnamic acid or 3,4-dihydroxy benzonitrile, corresponding to obtain four modified waste fibers (MWF1, MWF2, MWF3, and MWF4). The MWFs samples’ microstructure properties were characterized using SEM, EDS, XPS, FTIR analyses, and water contact angle tests. The results revealed that all the MWF surfaces were wrapped by a distinct coating layer and had different elemental compositions and chemical groups, demonstrating the significant effect of the four modifications on the WF surfaces. The hydroxyl, amino, or nitrile groups were grafted onto the WF surfaces causing improvement of the hydrophilicity and reactivity. Furthermore, all the MWFs as the reinforced materials were incorporated into the industrial waste phosphogypsum (PG) to manufacture the phosphorous-building gypsum composites (PBGC). The effects on the micro-morphology and mechanical properties of the PBGC were evaluated. The results also show the improvement in flexural and compressive strength with the addition of MWFs into the PBGC, due to the enhancement of the compactness between the MWF and phosphogypsum matrix. In particular, the effects of three compound modifiers on the flexural and compressive strength are more significant. The highest flexural and compressive strength was contributed by the PBGC-MWF4 with 2% dosage using a compound modifier of dopamine hydrochloride and 3,4-dihydroxy benzonitrile, which were enhanced 61.04% and 25.97% compared with the PBG.

In order to reduce the etching effect of the catalysts to carbon fibers caused by high temperature during the chemical vapor deposition (CVD) process, four multi-element catalysts, Fe–Co, Fe–Ni, Co–Ni and Fe–Co–Ni, were used to realize the low temperature growth of carbon nanotubes (CNTs) on carbon fibers at 350 °C–400 °C. The results show that the growth state of CNTs has a great relationship with the type of catalysts. The catalytic efficiency of Fe–Co catalysts is low, but the graphitization degree of CNTs is relatively high. The Fe–Co–Ni catalysts has high catalytic efficiency but low graphitization degree of CNTs. The tensile strength of carbon fiber/CNTs reinforcements prepared by Fe–Ni catalysts at 400 °C is the highest, reaching 3.99 GPa, which is 11.14% higher than that of desized fiber. The melt drop phenomenon of the catalysts was found by TEM, indicating the formation of the liquid phase catalysts during the growth of CNTs. This phenomenon can change the diffusion mode of carbon atoms in the catalyst and significantly reduce the growth activation energy of CNTs, so that CNTs can grow at lower temperatures. Based on the detailed analysis of the CVD process, a low temperature growth model of CNTs on carbon fibers was proposed.