Reversed austenite is of vital importance in low-carbon martensitic stainless steel because it improves impact toughness. However, a proper amount of reversed austenite is obtained by tempering at a critical temperature, which reduces the strength of the steel. Therefore, how to improve strength–toughness matching is an important problem. Copper (Cu) is an effective strengthening element in steels. However, there is little in-depth discussion on the role of Cu on the microstructure and mechanical properties of low-carbon martensite steel. In this work, the effect of different Cu content on the reversed austenite formation, tensile strength, and impact toughness of a low-carbon martensitic stainless steel (0Cr13Ni4Mo) was systematically investigated through use of a transmission electron microscope (TEM), transmission Kikuchi diffraction (TKD), atom probe tomography (APT), and other characterization methods and mechanical property tests. The results showed that the addition of Cu decreased the phase transition temperatures of martensite and austenite and increased the volume fraction of the reversed austenite. APT results indicated that Cu-rich clusters first formed with alloying elements such as ferrum (Fe) and nickel (Ni) and then grew to be precipitates through rejection of the alloying elements. The Ni atoms diffused towards the interface between the precipitates and the martensite matrix, which provided heterogeneous nucleation sites for the reversed austenite. Cu precipitations strengthened tensile strength during tempering. However, it generated temper brittleness in the steel at a tempering temperature of 450 °C, resulting in the impact energy of the 3Cu-steel being only 7 J. A good combination with higher tensile strength (863 MPa) and ductility (192 J) was obtained when tempering at 600 °C in the presence of Cu-rich precipitates and a sufficient volume fraction of the reversed austenite. The results provide guidance for the design of steels with reversed austenite and Cu and promote the development of high-strength and high-toughness steels.

Natural aging (NA) is unavoidable in Al-Mg-Si alloys during actual manufacturing. Revealing the reasons for the alloy strength reduction caused by the negative NA effect is of great significance to research and practice. In this work, atom probe tomography (APT) and transmission electron microscopy (TEM) were employed simultaneously to study the effect of NA on precipitates and their contributions to the strength of Al-Mg-Si alloys. It was found that the numerous clusters formed after significant NA are unstable and will dissolve into the matrix during initial AA. However, a few stable clusters are undissolved and will result in abnormal growth of β″, which then transforms to β′. Due to the decrease of nucleation sites resulting from the abnormal growth of precipitates, more solute atoms remain in the matrix. The calculation results show that the strengthening of the solid solution atoms is much smaller than that of large-sized β′, which is much less than that of fine β″. Therefore, lengthy NA causes a significant reduction in AA strength of the Al-Mg-Si alloy.