All human tissues present with unique mechanical properties critical to their function. This is achieved in part through the specific architecture of the extracellular matrix (ECM) fibres within each tissue. An example of this is seen in the walls of the vasculature where each layer presents with a unique ECM orientation critical to its functions. Current adopted vascular grafts to bypass a stenosed/damaged vessel fail to recapitulate this unique mechanical behaviour, particularly in the case of small diameter vessels (<6 mm), leading to failure. Therefore, in this study, melt-electrowriting (MEW) was adopted to produce a range of fibrous scaffolds to mimic the extracellular matrix (ECM) architecture of the tunica media of the vasculature, in an attempt to match the mechanical and biological behaviour of the native porcine tissue. Initially, the range of collagen architectures within the native vessel was determined, and subsequently replicated using MEW (winding angles (WA) 45°, 26.5°, 18.4°, 11.3°). These scaffolds recapitulated the anisotropic, non-linear mechanical behaviour of native carotid blood vessels. Moreover, these grafts facilitated human mesenchymal stem cell (hMSC) infiltration, differentiation, and ECM deposition that was independent of WA. The bioinspired MEW fibre architecture promoted cell alignment and preferential neo-tissue orientation in a manner similar to that seen in native tissue, particularly for WA 18.4° and 11.3°, which is a mandatory requirement for long-term survival of the regenerated tissue post-scaffold degradation. Lastly, the WA 18.4° was translated to a tubular graft and was shown to mirror the mechanical behaviour of small diameter vessels within physiological strain. Taken together, this study demonstrates the capacity to use MEW to fabricate bioinspired scaffolds to mimic the tunica media of vessels and recapitulate vascular mechanics which could act as a framework for small diameter graft development to guide tissue regeneration and orientation.

This study investigates diffusion tensor imaging (DTI) for providing microstructural insight into changes in arterial tissue by exploring how cell, collagen and elastin content effect fractional anisotropy (FA), mean diffusivity (MD) and tractography. Five ex vivo porcine carotid artery models (n = 6 each) were compared—native, fixed native, collagen degraded, elastin degraded and decellularised. Vessels were imaged at 7 T using a DTI protocol with b = 0 and 800 s/mm²and 10 isotopically distributed directions. FA and MD were evaluated in the vessel media and compared across models. FA values measured in native (p < 0.0001), fixed native (p < 0.0001) and collagen degraded (p = 0.0018, p = 0.0016, respectively) were significantly higher than those in elastin degraded and decellularised arteries. Native and fixed native had significantly lower MD values than elastin degraded (p < 0.0001) and decellularised tissue (p = 0.0032, p = 0.0003, respectively). Significantly lower MD was measured in collagen degraded compared with the elastin degraded model (p = 0.0001). Tractography yielded helically arranged tracts for native and collagen degraded vessels only. FA, MD and tractography were found to be highly sensitive to changes in the microstructural composition of arterial tissue, specifically pointing to cell, not collagen, content as the dominant source of the measured anisotropy in the vessel wall.

Non-invasive microstructural characterisation has the potential to determine the stability, or lack thereof, of atherosclerotic plaques and ultimately aid in better assessing plaques’ risk to rupture. If linked with mechanical characterisation using a clinically relevant imaging technique, mechanically sensitive rupture risk indicators could be possible. This study aims to provide this link–between a clinically relevant imaging technique and mechanical characterisation within human atherosclerotic plaques. Ex vivo diffusion tensor imaging, mechanical testing, and histological analysis were carried out on human carotid atherosclerotic plaques. DTI-derived tractography was found to yield significant mechanical insight into the mechanical properties of more stable and more vulnerable microstructures. Coupled with insights from digital image correlation and histology, specific failure characteristics of different microstructural arrangements furthered this finding. More circumferentially uniform microstructures failed at higher stresses and strains when compared to samples which had multiple microstructures, like those seen in a plaque cap. The novel findings in this study motivate diagnostic measures which use non-invasive characterisation of the underlying microstructure of plaques to determine their vulnerability to rupture.Graphic abstract

Background: This study aims to address the potential of ex vivo diffusion tensor imaging to provide insight into the microstructural composition and morphological arrangement of aged human atherosclerotic carotid arteries. Methods: In this study, whole human carotid arteries were investigated both anatomically and by comparing healthy and diseased regions. Nonrigid image registration was used with unsupervised segmentation to investigate the influence of elastin, collagen, cell density, glycosaminoglycans, and calcium on diffusion tensor imaging derived metrics (fractional anisotropy and mean diffusivity). Early stage atherosclerotic features were also investigated in terms of microstructural components and diffusion tensor imaging metrics. Results: All vessels displayed a dramatic decrease in fractional anisotropy compared with healthy animal arterial tissue, while the mean diffusivity was sensitive to regions of advanced disease. Elastin content strongly correlated with both fractional anisotropy (r>0.7, P −0.79, P <0.0002), and the thickened intima was also distinguishable from arterial media by these metrics. Conclusions: These different investigations point to the potential of diffusion tensor imaging to identify characteristics of arterial disease progression, at early and late-stage lesion development.

Purpose: To characterize microstructural contributions to the magnetic susceptibility of carotid arteries.Method: Arterial vessels were scanned using high‐resolution quantitative susceptibility mapping (QSM) at 7 Tesla. Models of vessel degradation were generated using ex vivo porcine carotid arteries that were subjected to several different enzymatic digestion treatments that selectively removed microstructural components (smooth muscle cells, collagen, and elastin). Magnetic susceptibilities measured in these tissue models were compared to those in untreated (native) porcine arteries. Magnetic susceptibility measured in native porcine carotid arteries was further compared to the susceptibility of cadaveric human carotid arteries to investigate their similarity.Results: The magnetic susceptibility of native porcine vessels was diamagnetic (χ_native = −0.1820 ppm), with higher susceptibilities in all models of vessel degradation (χ_{elastin‐degraded} = −0.0163 ppm; χ_{collagen‐degraded} = −0.1158 ppm; χ_{decellularized} = −0.1379 ppm; χ_{fixed native} = −0.2199 ppm). Magnetic susceptibility was significantly higher in collagen‐degraded compared to native porcine vessels (Tukey‐Kramer, P < .01) and between elastin‐degraded and all other models (including native, Tukey‐Kramer, P < .001). The susceptibility of fixed healthy human arterial tissue was diamagnetic, and no significant difference was found between fixed human and fixed porcine arterial tissue susceptibilities (analysis of variance, P > .05).Conclusions: Magnetic susceptibility measured using QSM is sensitive to the microstructural composition of arterial vessels—most notably to collagen. The similarity of human and porcine arterial tissue susceptibility values provides a solid basis for translational studies. Because vessel microstructure becomes disrupted during the onset and progression of carotid atherosclerosis, QSM has the potential to provide a sensitive and specific marker of vessel disease.

Aortic aneurysms (AA) occur in 4.8% of people causing 150,000 deaths annually. While endovascular aneurysm repairs reduce surgical morbidity, device-related failures (leak/displacement) are frequent highlighting the need for test models that better represent the mural geometry and compliance changes in human AAs. We aimed to develop and characterise an ex vivo porcine aortic model of AA. The optimal duration of tissue elastase exposure to emulate AA changes in elastin microstructure and content was determined using porcine aortic rings. Elastase-induced changes were quantified morphologically, and mechanical properties assessed via ring tensile testing. Subsequent experiments tested the potential for localised elastase treatment in a 1 cm segment of porcine aorta using a specially designed 3D printed rig. The effect on pressure-diameter behaviour was investigated via inflation-extension testing. Elastase treatment produced time dependent decreases in elastin, resulting in an increased tensile modulus and circumferential length in the ring samples in the final phase of the J-shaped tissue stress-strain curves. In whole aortic segments, localised elastase-induced luminal degradation was successfully limited to a central region. The degree of elastin degradation achieved was sufficient to cause localised dilation with respect to controls under physiological pressures. Localised elastin degradation in porcine aortic segments is feasible and emulates the changes seen clinically in aortic aneurysms.