The utilizing of traditional chemical stabilizers could improve soil engineering properties but also results in brittle behavior and causes environmental problems. This study investigates the feasibility of the combined utilization of an ecofriendly biopolymer and fiber inclusions as an alternative to traditional cement for reinforcing soft soil. A series of unconfined compression tests were conducted to examine the combined effect of the biopolymer and fibers on the stress–strain characteristics, strength improvement, failure pattern, and reinforcement mechanism of soft soil. The results show that the biopolymer associated with fibers has an unconfined compressive strength similar to that of fiber-reinforced soil. However, it then increases with different curing times and conditions, which can be up to 1.5 MPa–2.5 MPa. The combined effect of fibers and the biopolymer is not simply equivalent to the sum of the effects of each individual material. The fiber shows its role instantly after being mixed into soil, whereas the effect of biopolymer gradually appears with sample curing time. The biopolymer plays a dominant role in increasing the peak unconfined compressive strength and brittleness of soil, while the amount of fiber is crucial for reducing soil brittleness and increasing ductility. It is shown that the biopolymer not only contributes to the particle bonding force but also facilitates the reinforcement efficiency of fibers in the soil. The fibers in return assist in reducing the soil brittleness arising from biopolymer cementation and provide residual resistance after post-peak failure.

The study of the high-performance of biopolymers and current eco-friendly have recently emerged. However, the micro-behavior and underlying mechanisms during the test are still unclear. In this study, we conducted experimental and numerical tests in parallel to investigate the impact of different xanthan gum biopolymer contents sand. Then, a numerical simulation of the direct tensile test under different tensile positions was carried out. The micro-characteristics of the biopolymer-treated sand were captured and analyzed by numerical simulations. The results indicate that the biopolymer can substantially increase the uniaxial compressive strength and tensile strength of the soil. The analysis of the microparameters demonstrates the increase in the contact bond parameter values with different biopolymer contents, and stronger bonding strength is provided with a higher biopolymer content from the microscale. The contact force and crack development during the test were visualized in the paper. In addition, a regression model for predicting the direct tensile strength under different tensile positions was established. The numerical simulation results explained the mechanical and fracture behavior of xanthan gum biopolymer stabilized sand under uniaxial compression, which provides a better understanding of the biopolymer strengthening effect.

A rapid growth in the population leads to a large increase in engineering construction. This means there is an inevitability in regard to building on problematic soils. Soil reinforcement becomes an important subject due to the fact that it is a concern for engineers and scientists. With the development of nanotechnology, more and more nanomaterials are being introduced within the practice of soil reinforcement engineering. In this study, the reinforcing effect of novel nanomaterial nano-silica (SiO₂) applied to different kinds of soils was systematically studied. The nano-SiO₂-reinforced soil possessed lower final water evaporation loss, and evaporation rates. The nano-SiO₂ increased the shear strength of clayey soil and sandy soil under both cured and uncured conditions, but the reinforcing effect on clayey soil was more obvious. The addition of nano-SiO₂ promotes the friction angle and cohesion of clayey soil; further, it also increases the cohesion of sandy soil. The unconfined compressive strength of clayey soil was enhanced by nano-SiO₂, meanwhile, the nano-SiO₂-reinforced soil possessed greater brittleness. The microstructure of nano-SiO₂-reinforced soil is shown via SEM analysis, and the results of X-ray diffraction (XRD) tests show that there are no new mineral components generated during the reinforcing process. It was also found that nano-SiO₂ possessed little influence on the soil pH value. Adding nano-SiO₂ will not damage the original chemical environment of the soil. The microstructure of nano-SiO₂-reinforced soil was observed to prove the results above. In general, nano-SiO₂ is an excellent soil additive that can improve the mechanical properties of both clayey soil and sandy soil effectively. This research provides more ideas and directions for the purposes of selecting soil reinforcement materials.