Although the activating effect of an acetate medium in the cold sintering process of zinc oxide ceramics is well known, some problems need to be solved on the effect of process conditions and the initial powder’s preparation methods on the ceramic’s density and microstructure. This article describes an effect of the zinc acetate introduction method, its concentration in zinc oxide powder as well as that of the die sealing configuration on the density and microstructure of zinc oxide ceramics obtained by the cold sintering process at 244 °C. The activating additive of zinc acetate was applied in two ways: (1) impregnation in aqueous solution and (2) impregnation with subsequent treatment in water vapor. Zinc oxide powders and ceramics were analyzed using SEM, TGA/DSC/MS and XRD to reveal the effect of powder pre-treatment and sintering conditions on the material microstructure. Cold sintered ZnO ceramics samples with a relative density up to 0.99 and with average grain sizes from 0.28 to 1.71 μm were obtained. The die sealing by two Teflon sealing rings appeared to be the most effective.

— Solid-state transformations of a 3[Pd(NH3)4]Cl2 + (NH4)2CrO4mixture at temperatures from 40 to 550°C in various media have been studied by thermal analysis and mass spectrometry. The...

Sequential thermal transformations of a 3[Pd(NH3)4]Cl2–2(NH4)2Cr2O7mixture (Pd : Cr molar ratio, 3 : 4) are studied via thermal analysis and mass spectrometry in an argon atmosphere and the...

The influence of the method of applying the activating additive ammonium chloride and its concentration on the density and microstructure of zinc oxide ceramic obtained by cold sintering at 244 °C was investigated. The activating agent was applied by two methods: impregnation and subsequent autoclave treatment. When the powder was activated by the impregnation method, the crystal sizes remained at the initial level of 0.17–0.19 μm. After the autoclave treatment, the crystal sizes increased to 0.31–0.53 μm. Samples of cold sintering ZnO with relative density up to 0.96 and average grain sizes 0.29–0.86 μm were obtained. ZnO powders and ceramic samples were analyzed using SEM, TGA/DSC, and XRD to reveal the effect of the powder activation method and cold sintering conditions on the material microstructure. The effect of ammonium chloride concentration on grain growth and microstructure of ceramic samples is shown. It was found that the average grain size of ceramic samples with an increase in additive concentration passes through a minimum. In cold sintering of the autoclave activated powder, the effect of reducing the average grain size was observed. The results of this work are discussed on the basis of the idea of the solid-phase mobility of the crystal structure arising when interacting with an aqueous medium.

The rhenium- and ruthenium-containing catalysts are active in the oxidation of CH _x and CO and in the reduction of NO _x . Comparative testing of catalyst samples under laboratory conditions and on an engine stand demonstrated that these catalysts outperform the known commercial catalysts in the neutralization of exhaust gas from automotive gasoline engines. It is, therefore, possible to completely replace expensive Rh and partially replace Pt and Pd with cheaper components—Re and Rh—in the manufacturing of catalytic converters.