The activity of stem cell processes is regulated by internal and external signals of the cell “niche”. In general, the niche of stem cells can be represented as the microenvironment of the cells, providing a signal complex, determining the properties of the cells. At the same time, the “niche” concept implies feedback. Cells can modify their microenvironment, supporting homeostasis or remodeling the composition and structure of the extracellular matrix. To ensure the regenerative potential of tissue engineering products the “niche” concept should be taken into account. To investigate interactions in an experimental niche, an original hydrogel biopolymer scaffold with encapsulated mesenchymal adipose-derived stem cells (ASCs) was used in this study. The scaffold provides for cell adhesion, active cell growth, and proliferative activity. Cells cultured within a scaffold are distinguished by the presence of a developed cytoskeleton and they form a cellular network. ASCs cultured within a scaffold change their microenvironment by secreting VEGF-A and remodeling the scaffold structure. Scaffold biodegradation processes were evaluated after previous culturing of the ASCs in the scaffolds for periods of either 24 h or six days. The revealed differences confirmed that changes had occurred in the properties of scaffolds remodeled by cells during cultivation. The mechanisms of the identified changes and the possibility of considering the presented scaffold as an appropriate artificial niche for ASCs are discussed.

The success of the regenerative process resulting from the implantation of a scaffold or a tissue-engineered structure into damaged tissues depends on a series of factors, including, crucially, the biodegradability of the implanted materials. The selection of a scaffold with appropriate biodegradation characteristics allows for synchronization of the degradation of the construct with the processes involved in new tissue formation. Thus, it is extremely important to characterize the biodegradation properties of potential scaffold materials at the stage of in vitro studies. We have analyzed the biodegradation of hybrid fibrin–collagen scaffolds in both PBS solution and in trypsin solution and this has enabled us to describe the processes of both their passive and enzymatic degradation. It was found that the specific origin of the collagen used to form part of the hybrid scaffolds could have a significant effect on the nature of the biodegradation process. It was also established, during comparative studies of acellular scaffolds and scaffolds containing stem cells, that the cells, too, make a significant contribution to changes in the biodegradation and structural properties of such scaffolds. The study results also provided evidence indicating the dependency between the pre-cultivation period for the cellular scaffolds and the speed and extent of their subsequent biodegradation. Our discussion of results includes an attempt to explain the mechanisms of the changes found. We hope that the said results will make a significant contribution to the understanding of the processes affecting the differences in the biodegradation properties of hybrid, biopolymer, and hydrogel scaffolds.

Porous polymer monoliths with thicknesses of 2 and 4 mm were obtained via polymerization of ethylene glycol dimethacrylate (EGDMA) under the influence visible-light irradiation in the presence of a 70 wt% 1-butanol porogenic agent and o-quinone photoinitiators. The o-quinones used were: 3,5-di-tret-butyl-benzoquinone-1,2 (35Q), 3,6-di-tret-butyl-benzoquinone-1,2 (36Q), camphorquinone (CQ), and 9,10-phenanthrenequinone (PQ). Porous monoliths were also synthesized from the same mixture but using 2,2′-azo-bis(iso-butyronitrile) (AIBN) at 100 °C instead o-quinones. According to the results of scanning electron microscopy, all the resulting samples were conglomerates of spherical, polymeric particles with pores between them. Use of mercury porometry showed that the interconnected pore systems of all the polymers were open. The average pore size, D_mod, in such polymers strongly depended on both the nature of the initiator and the method of initiation of polymerization. For polymers obtained in the presence of AIBN, the D_mod value was as low as 0.8 μm. For polymers obtained via photoinitiation in the presence of 36Q, 35Q, CQ, and PQ, the D_mod values were significantly greater, i.e., 9.9, 6.4, 3.6, and 3.7 μm, respectively. The compressive strength and Young’s modulus of the porous monoliths increased symbatically in the series PQ < CQ < 36Q < 35Q < AIBN with decreasing proportions of large pores (over 12 μm) in their polymer structures. The photopolymerization rate of the EGDMA and 1-butanol, 30:70 wt% mixture was maximal for PQ and minimal for 35Q. All polymers tested were non-cytotoxic. Based on the data from MTT testing, it can be noted that the polymers obtained via photoinitiation were characterized by their positive effect on the proliferative activity of human dermal fibroblasts. This makes them promising osteoplastic materials for clinical trials.

The most difficult issue when using tissue engineering products is enabling the ability to store them without losing their restorative capacity. The numbers and viability of mesenchymal stem cells encapsulated in a hydrogel scaffold after cryostorage at −80 °C (by using, individually, two kinds of cryoprotectors—Bambanker and 10% DMSO (Dimethyl sulfoxide) solution) for 3, 6, 9, and 12 months were determined, with subsequent assessment of cell proliferation after 96 h. The analysis of the cellular component was performed using fluorescence microscopy and the two fluorochromes—Hoechst 3334 and NucGreenTM Dead 488. The experimental protocol ensured the preservation of cells in the scaffold structure, retaining both high viability and proliferative activity during storage for 3 months. Longer storage of scaffolds led to their significant changes. Therefore, after 6 months, the proliferative activity of cells decreased. Cryostorage of scaffolds for 9 months led to a decrease in cells’ viability and proliferative activity. As a result of cryostorage of scaffolds for 12 months, a decrease in viability and proliferative activity of cells was observed, as well as pronounced changes in the structure of the hydrogel. The described scaffold cryostorage protocol could become the basis for the development of storage protocols for such tissue engineering products, and for helping to extend the possibilities of their clinical use while accelerating their commercialization.