The gamma radiation shielding ability for CaO-K₂O-Na₂O-P₂O₅ glasses were experimentally determined between 0.0595 and 1.41 MeV. The experimental MAC results were compared with theoretical results obtained from the XCOM software to test the accuracy of the experimental values. Additionally, the effect of increasing the P₂O₅ in the glass composition, or reducing the Na₂O content, was evaluated at varying energies. For the fabricated glasses, the experimental data strongly agreed with the XCOM results. The effective atomic number (Z_eff) of the fabricated glasses was also determined. The Z_eff values start out at their maximum (12.41–12.55) at the lowest tested energy, 0.0595 MeV, and decrease to 10.69–10.80 at 0.245 MeV. As energy further increases, the Z_eff values remain almost constant between 0.344 and 1.41 MeV. The mean free path (MFP) of the fabricated glasses is investigated and we found that the lowest MFP value occurs at the lowest tested energy, 0.0595 MeV, and lies within the range of 1.382–1.486 cm, while the greatest MFP can be found at the highest tested energy, 1.41 MeV, within the range of 8.121–8.656 cm. At all energies, the KCNP40 sample has the lowest MFP, while the KCNP60 sample has the greatest. The half value layer (HVL) for the KCNP-X glasses is determined. For all the selected energies, the HVL values follow the order of KCNP40 < KCNP45 < KCNP50 < KCNP55 < KCNP60. The HVL of the KCNP50 sample increased from 0.996 to 2.663, 3.392, 4.351, and 5.169 cm for energies of 0.0595, 0.245, 0.444, 0.779, and 1.11 MeV, respectively. The radiation protection efficiency (RPE) results reveal that decreasing the P₂O₅ content in the glasses improves the radiation shielding ability of the samples. Thus, the KCNP40 sample has the best potential for photon attenuation applications.

Polymers are often used in medical applications, therefore, some novel polymers and their interactions with photons have been studied. The gamma-ray shielding parameters for Polymethylpentene (PMP), Polybutylene terephthalate (PBT), Polyoxymethylene (POM), Polyvinylidenefluoride (PVDF), and Polychlorotrifluoroethylene (PCTFE) polymers were determined using the Geant4 simulation and discussed in the current work. The mass attenuation coefficients (μ/ρ) were simulated at low and high energies between 0.059 and 1.408 MeV using different radionuclides. The accuracy of the Geant4 simulated results were checked with the XCOM software. The two different methods had good agreement with each other. Exposure buildup factor (EBF) was calculated and discussed in terms of polymers under study and photon energy. Effective atomic number (Z_eff) and electron density (N_eff) were calculated and analyzed at different energies. Additionally, the half-value layer (HVL) of the polymers was evaluated, and the results of this parameter showed that PCTFE had the highest probability of interaction with gamma photons compared to those of the other tested polymers.

Aiming to extend the scope of utilizing glass in radiation shielding, this work investigates the radiation interaction response of a borate-based glass system. Four borate-glass samples of different substituting concentrations of calcium oxide ( $$70-x$$70 - x )B₂O₃: $$10$$10 Na₂O $$:5$$: 5 Al₂O₃ $$:15$$: 15 BaO: $$x$$x CaO were prepared. To assess the shielding performance of the prepared glass samples, a high-purity germanium detector and different radioactive sources (different energies) were used. Via the narrow beam method, the linear attenuation coefficients (LACs) were experimentally measured. So, the transmission factor (TF), the half-value layer (HVL), the tenth value layer (TVL), the mean free path (MFP), and the radiation protection efficiency (RPE) were calculated for all prepared samples. It was observed that the increase of the concentration of calcium oxide in the proposed borate-based glass samples leads to improve their performance in shielding against radiation. At low energy, the RPE of the samples is almost 100%. However, it was observed that as energy of the radiation source increases, the shielding performance of the samples will decrease. High energy dependence was found when calculating TF, HVL, TVL, and MFP. They were increased with the increase of the energy of the incident photons. At 0.662 MeV, the TF values are equal to 79.26, 79.00, 79.72, and 78.43% for BNABC-1, BNABC-2, BNABC-3, and BNABC-4 in the same oder, respectively. The application of the proposed composition of borate-based glass as a transparent shield against low-energy ionizing radiation was highlighted.