Molten salt electrodeposition is the process of producing impressively dense deposits of refractory metals using the electrolysis of molten salts. However, predicting which electrochemical parameters and setup will best control different kinds of deposition (density, homogeneity, etc.) is an ongoing challenge, due to our limited understanding of the properties and mechanisms that drive molten salt electrodeposition. Because these advancements have been made rapidly and in different arenas, it is worth taking the time to stop and assess the progress of the field as a whole. These advancements have increasing relevance for the energy sector, the development of space materials and engineering applications. In this review, we assess four critical facets of this field: (1) how the current understanding of process variables enhances the electrodeposition of various molten salts and the quality of the resulting product; (2) how the electrochemical setup and the process parameters (e.g., cell reactions) are known to impact the electrodeposition of different metal coatings and refractory-metal coatings; (3) the benefits and drawbacks of non-aqueous molten salt electrodeposition, and (4) promising future avenues of research. The aim of this work is to enhance our understanding of the many procedures and variables that have been developed to date. The expectation is that this review will act as a stimulant, motivating scientists to delve further into the investigation of refractory-metal alloys by utilizing molten salt electrodeposition.

Carburization of cladding materials has long been a concern for the nuclear industry and has led to the restricted use of high-thermal conductivity fuels such as uranium carbides. With the rise of small modular reactors (SMRs) that frequently implement a graphite core-block, carburization of reactor components is once more in the foreground as a potential failure mechanism. To ensure commercial viability for SMRs, neutron-friendly cladding materials such as Zr-based alloys are required. In this work, the carburization kinetics of Zircaloy-4 (Zry-4), for the temperature range 1073–1673 K (covering typical operating temperatures and off-normal scenarios) are established. The following Arrhenius relationship for the parabolic constant describing ZrC growth is derived: K_p (in μm²/s) = 609.35 exp(−1.505 × 10⁵/RT)). Overall, the ZrC growth is sluggish below 1473 K which is within the operational temperature range of SMRs. In all cases the ZrC that forms from solid state reaction is hypo-stoichiometric, as confirmed through XRD. The hardness and elastic modulus of carburized Zry-4 are also examined and it is shown that despite the formation of a ZrC layer, C ingress in the Zry-4 bulk does not impact the mechanical response after carburization at 1073 K and 1473 K for 96 h.