Externally bonded carbon-fiber-reinforced polymer (CFRP) technology can be used by different methods based on the anchorage device, CFRP type, and prestressing/nonprestressing. However, a direct comparison between the strengthening efficacies of different methods is still lacking. Seven large-scale RC beams were tested in this study to investigate the influences of the anchorage method, CFRP type, prestress, and prestressing system on the flexural strengthening efficacy of RC beams. The test results showed that the ultimate load increased by 38.3%, whereas the cracking and yielding loads were slightly affected when the anchorage method was enhanced from CFRP U-wraps to wedge-clamp anchors. The CFRP plate and CFRP sheet could provide a rather close flexural strengthening efficacy under the same CFRP strengthening amount. Compared to the nonprestressed CFRP plate, the prestressed CFRP plate was highly superior in improving the flexural behavior of RC beams. The cracking, yielding, and ultimate loads of the prestressed CFRP-strengthened specimens were 57.1%, 22.9%, and 5.9%, respectively, higher than those of the nonprestressed CFRP-strengthened specimen with an effective anchorage. The two types of prestressing systems based on the adhesive-friction anchor and wedge-clamp anchor were proven to be effective for flexural strengthening of RC beams with prestressed CFRP plates, and they could provide almost the same strengthening effect.

The surface modification of aramid fiber plain fabric (PPTA) was conducted through phthalic anhydride treatment and anhydrous aluminum chloride (AlCl₃) catalysis, aiming to enhance the interfacial bonding strength between aramid fiber fabric and bisphenol A diglycidyl ether (DGEBA) resin. The surface morphologies and structures of PPTA fiber before and after modification were characterized using scanning electron microscopy, atomic force microscopy, X-ray photoelectron spectroscopy, and X-ray diffractometry. The mechanical properties of the PPTA/DGEBA composite were evaluated using a universal mechanical testing machine. The results demonstrate that when the concentration of phthalic anhydride is 0.3 mol/L, the tensile strength, bending strength and interlaminar shear strength of PPTA/DGEBA composites reach the maximum value, which are increased by 17.94%, 44.18%, and 15.94% compared with the unmodified sample, respectively. After a 0.5-h catalytic modification, the PPTA/DGEBA composites exhibited significantly enhanced tensile strength, bending strength, and interlaminar shear strength, achieving respective increments of 32.28%, 24.91%, and 29.10% compared to the modified samples without catalyst addition. Moreover, the overall mechanical properties of the aramid fiber fabrics and composites were substantially improved, which are more suitable for structural applications.

This study introduces an innovative wedge anchor for double-layer carbon fiber reinforced polymer (CFRP) plate cable to address the current limitation of traditional wedge anchors. By employing the design concept of “secondary force transmission path”, the friction force for anchoring the CFRP plate is effectively transferred into the barrel through its contracting wedge, thus reducing the clamping pressure requirement of traditional wedge anchorage for anchoring thick or double-layer CFRP plates. Based on this conception, this study presents a theoretical analysis model for predicting the influence of parameter variations on the compressive stress of the CFRP plate, which can serve as a tool for rapid configuration preliminary design. Through finite element analysis, the internal stress distribution of the anchor is thoroughly investigated, and the theoretical analysis model for fast predicting compressive stress of CFRP plate is also validated. The results also indicate that the anchorage conception is valid and effective, providing sufficient anchorage of CFPR plates with an anchorage length of 100 mm.

The use of carbon fiber reinforced polymer (CFRP) strands as prestressed reinforcement in prestressed concrete (PC) structures offers an effective solution to the corrosion issues associated with prestressed steel strands. In this study, the flexural behavior of PC beams reinforced with prestressed CFRP strands and non-prestressed steel rebars was investigated using finite element modeling (FEM) and artificial neural network (ANN) methods. First, three-dimensional nonlinear FE models were developed. The FE results indicated that the predicted failure mode, load-deflection curve, and ultimate load agreed well with the previous test results. Variations in prestress level, concrete strength, and steel reinforcement ratio shifted the failure mode from concrete crushing to CFRP strand fracture. While the ultimate load generally increased with a higher prestressed level, an excessively high prestress level reduced the ultimate load due to premature fracture of CFRP strands. An increase in concrete strength and steel reinforcement ratio also contributed to a rise in the ultimate load. Subsequently, the verified FE models were utilized to create a database for training the back propagation ANN (BP-ANN) model. The ultimate moments of the experimental specimens were predicted using the trained model. The results showed the correlation coefficients for both the training and test datasets were approximately 0.99, and the maximum error between the predicted and test ultimate moments was around 8%, demonstrating that the BP-ANN method is an effective tool for accurately predicting the ultimate capacity of this type of PC beam.