This paper proposes the development of a novel coagulant for dust suppression in open-cast mines. Specifically, pretreated sodium lignin sulfonate and acrylic acid were first cross-linked, then the graft copolymerization of the intermediate product (the cross-linking product) and acrylamide was conducted and finally the resulting gelatinous substances were crushed. During the reaction process, N,N’-methylene-bis-acrylamide and ammonium persulfate were used as the cross-linking agent and initiator, respectively. Subsequently, the functional groups, crystalline structure, and thermal stability of the dust coagulant were examined by means of Fourier transform infrared spectra measurements, X-ray diffraction spectra measurements, and differential scanning calorimeter analysis. Moreover, single-factor experiments were conducted to explore the optimal synthesis condition. According to the experimental results, the coagulant achieved its optimal dust suppression performance under the following conditions: the mass ratio of lignin to acrylic acid was 1:3, the mass ratio of lignin to acrylamide was 2:7, the content of the cross-linking agent was 0.9%, the mass ratio of initiator to acrylamide was 2:100, the reaction temperature was set as 60℃, and the pH value was set as 7. Finally, the coagulant was measured for its swelling kinetics, viscosity, film-forming hardness, peeling strength, and ability to suppress dust. It can be concluded that the coagulant exhibits a very high standard of both dust suppression and wind resistance.

The coal industry plays an essential role in China’s economic development, and issues such as occupational health and environmental pollution caused by coal dust have attracted a great deal of attention. In accordance with the principles of environmental protection and waste management, this study used carboxymethyl ginkgo cellulose (CL) extracted and modified from Ginkgo biloba leaves as a matrix, and a graft copolymerized with sodium 3-allyloxy-1-hydroxy-1-propanesulfonate (AHPS) and N-isopropylacrylamide (NIPAM) monomers to prepare low-cost, environmentally friendly, and high-performance coal dust suppression (C-A-N). By optimizing fitting experimental data through three factors and two response surface analyses, the optimal dust suppression efficiency ratio was determined to be 4:8:5, and its swelling and water retention properties were analyzed. The microstructure, chemical reaction process, combustion performance and crusting property of the dust suppression gel were analyzed using Fourier-transform infrared spectroscopy (FTIR), X-ray diffraction (XRD), thermogravimetry (TG), scanning electron microscopy (SEM), cone calorimetry, and consolidation layer strength tests. Relevant experiments show that the dust suppression gel prepared in this study has the characteristics of a strong wettability and minor impacts on the calorific value of coal, as well as green and environmental protection. When the wind speed is 10 m/s, the dust suppression effect reaches 93%, and the hardness of the solidified layer reaches 39.6 KPa. This study analyzed the migration and combination of functional groups in the interaction system using molecular dynamics simulation software. The microscopic effect and mechanism between dust suppression gel and coal are revealed from a molecular point of view. The feasibility and accuracy of the molecular dynamics simulation were verified by the consistency between simulation results and experimental data. Therefore, combining the utilization of waste resources with dust suppression can have important economic and social benefits.