Soy protein isolate (SPI) based films have received considerable attention for use in packaging materials. However, SPI-based films exhibit relatively poor mechanical properties and water resistance ability. To tackle these challenges, chitosan (CS) and endogenous Cu nanoclusters (NCs) capped with protein were proposed and designed to modify SPI-based films. Attenuated total reflectance-Fourier transform infrared spectroscopy and X-ray diffraction patterns of composite films demonstrated that interactions, such as hydrogen bonds in the film forming process, promoted the cross-linking of composite films. The surface microstructure of CS/SPI films modified with Cu NCs was more uniform and transmission electron microscopy (TEM) showed that uniform and discrete clusters were formed. Compared with untreated SPI films, the tensile strength and elongation at break of composite films were simultaneously improved by 118.78% and 74.93%, respectively. Moreover, these composite films also exhibited higher water contact angle and degradation temperature than that of pure SPI film. The water vapor permeation of the modified film also decreased. These improved properties of functional bio-polymers show great potential as food packaging materials.

Soy protein isolate (SPI)-based materials are abundant, biocompatible, renewable, and biodegradable. In order to improve the tensile strength (TS) of SPI films, we prepared a novel composite film modified with microcrystalline cellulose (MCC) and metal nanoclusters (NCs) in this study. The effects of the modification of MCC on the properties of SPI-Cu NCs and SPI-Zn NCs films were investigated. Attenuated total reflectance-Fourier transformed infrared spectroscopy analyses and X-ray diffraction patterns characterized the strong interactions and reduction of the crystalline structure of the composite films. Scanning electron microscopy (SEM) showed the enhanced cross-linked and entangled structure of modified films. Compared with an untreated SPI film, the tensile strength of the SPI-MCC-Cu and SPI-MCC-Zn films increased from 2.91 to 13.95 and 6.52 MPa, respectively. Moreover, the results also indicated their favorable water resistance with a higher water contact angle. Meanwhile, the composite films exhibited increased initial degradation temperatures, demonstrating their higher thermostability. The results suggested that MCC could effectively improve the performance of SPI-NCs films, which would provide a novel preparation method for environmentally friendly SPI-based films in the applications of packaging materials.

Wood composites used in indoor living environments often pose formaldehyde emission and fire hazard problems. In this study, magnesium oxychloride cement-based (MOC) inorganic adhesives are presented as an effective and sustainable binder for plywood applications. The phase composition, microstructure, and thermal stability of the adhesives prepared with different ratios of MgO/MgCl₂ were investigated. In addition, the dry and wet shear strength and the combustion behavior of the plywood were also examined. The results indicated that the limiting oxygen index (LOI) values of the plywood bonded by the MOC adhesives were higher than those of the plywood bonded by urea-formaldehyde resin. The active MgO/MgCl₂ molar ratio of 7 was the optimal ratio for the dry and wet shear strength of the plywood with values of 1.02 and 0.88 MPa, respectively, which meet the interior use panel (Type II plywood) requirements. These improvements were ascribed to the increasing ratio of MgO/MgCl₂ that facilitated the formation of an excellent microstructure. Meanwhile, the continuous hydration phase strengthened the interaction between the MOC adhesive and the wood. With these improved properties, MOC adhesive is expected to be widely used for industrial applications in plywood fabrication.