As cementation represents the last stage of the work involved in making various indirect restorations (metal ceramic crowns and bridges, full ceramic crowns and bridges, inlays, onlays, and fiber posts), its quality significantly contributes to the clinical success of the therapy performed. In the last two decades, the demand for ceramic indirect restorations in everyday dental practice has considerably increased primarily due to the growing significance of esthetics among patients, but also as a result of hypersensitivity reactions to dental alloys in some individuals. In this context, it is essential to ensure a permanent and reliable adhesive bond between the indirect restoration and the tooth structure, as this is the key to the success of aesthetic restorations. Resin-based luting materials benefit from excellent optical (aesthetic) and mechanical properties, as well as from providing a strong and durable adhesive bond between the restoration and the tooth. For this reason, resin cements are a reliable choice of material for cementing polycrystalline ceramic restorations. The current dental material market offers a wide range of resin cement with diverse and continually advancing properties. In response, we wish to note that the interest in the properties of resin-based cements among clinicians has existed for many years. Yet, despite extensive research on the subject and the resulting continued improvements in the quality of these materials, there is still no ideal resin-based cement on the market. The manuscript authors were guided by this fact when writing the article content, as the aim was to provide a concise overview of the composition, properties, and current trends, as well as some future guidelines for research in this field that would be beneficial for dental practitioners as well as the scientific community. It is extremely important to provide reliable and succinct information and guidelines for resin luting materials for dental dental practitioners.

Key advantages of Poly(methyl methacrylate)—PMMA for denture application are related to aesthetics and biocompatibility, while its main deficiency is related to mechanical properties. To address this issue, SiO₂ nanoparticle reinforcement was proposed, containing 0 to 5% nanosilica, to form nanocomposite materials. Flexural strengths and elastic moduli were determined and correlated to nominal nanoparticle content and zeta potential of the liquid phase nanoparticle solutions. Another issue is the biocompatibility, which was determined in terms of cytotoxicity, using L929 and MRC5 cell lines. The addition of nanoparticle was proved to be beneficial for increasing flexural strength and modulus, causing a significant increase in both strength and moduli. On the other hand, the formation of agglomerates was noted, particularly at higher nanoparticle loadings, affecting mechanical properties. The addition of nanosilica had an adverse effect on the cytotoxicity, increasing it above the level present in unmodified specimens. Cytotoxic potential was on the acceptable level for specimens with up to 2% nanosilica. Consequently, nanosilica proved to be an effective and biocompatible means of increasing the resistance of dental materials.

The degree of polymerization for dimethacrylate resin-based materials (BisGMA, TEGDMA, UDMA, HEMA) ranges from 55 to 75%. Literature data indicate that polymerization efficacy depends, among other factors, on the type of methacrylate resin comprising the material. The aim of this study was to evaluate the polymerization efficacy of four dental cement materials characterized by different polymerization mechanisms using FTIR analysis. In the present study, the FTIR method was adopted to analyze the degree of polymerization efficacy of four resin-based dental cement materials, two of which were self-cured and two were dual-cured cements. The IR spectral analysis was performed 24 h after the polymerization of the cementitious material. RelyX ARC cement exhibits the lowest polymerization efficacy (61.3%), while that of Variolink II (85.8%) and Maxcem Elite is the highest (90.1%). Although the efficacy of self-cured cements appears to be superior, the difference is not statistically significant (p = 0.280). Polymerization efficacy largely depends on the chemical structure of the material in terms of the presence of a particular methacrylate resin and less on the polymerization mechanism itself, i.e., whether it is a self-cured or dually cured dental cement. Thus, in clinical practice, cementitious materials with a higher proportion of TEGDMA compared with BisGMA are recommended.

(1) Background: The aim of this study was to investigate the agreement between a clinical diagnosis based on research diagnostic criteria/temporomandibular disorders (RDC/TMD) and high-field magnetic resonance imaging (MRI) findings of temporomandibular joints (TMJs) in asymptomatic females. (2) Methods: A prospective study on 100 females (200 TMJs) was performed, using clinical examinations (RDC/TMD) and same-day MRIs of TMJs on a 3T MR unit. The inclusion criteria were as follows: females, age > 18, the presence of upper and lower incisors, and an understanding of the Serbian language. Descriptive statistics (means and standard deviations) and ANOVA with a post hoc Tukey test for differences among the patient subgroups was performed. The agreement between the clinical and MRI findings was determined using Cohen’s kappa coefficient (k < 0.21 slight, 0.21–0.4 fair, 0.41–0.6 moderate, 0.61–0.8 substantial, and 0.81–1 almost perfect). The statistical significance was set at p ≤ 0.05. (3) Results: Normal findings were observed in 86.7%, disc dislocation (DD) was observed in 9.2%, and arthralgia/osteoarthritis/osteoarthrosis was observed in 2.6% of TMJs using RDC/TMD. On the MRI, normal findings were observed in 50.5%, disc dislocation was observed in 16.3%, and arthralgia/osteoarthritis/osteoarthrosis was observed in 23.5% of TMJs. The anterior DD with reduction showed fair agreement of the clinical and MRI findings (k = 0.240, p < 0.001) compared with the DD without reduction (k = 0.355, p < 0.001). Both showed high specificity (94.9% and 99.4%) but low sensitivity (24.2% and 25.0%). The sensitivity in osteoarthritic changes was low (4.8%), but the specificity remained high (96.2%). (4) Conclusions: The sensitivity of the clinical examination remains low compared with 3T MRI, especially in osteoarthritic changes and anterior DD with reduction. However, the number of false positive diagnoses using RDC/TMD is low in asymptomatic patients. RDC/TMD remains a sensible method for establishing a clinical diagnosis and avoiding the overtreatment of asymptomatic patients.

The paper presents the influence of impression methods, polymer materials, and implant angulation on the accuracy of the definitive working model for the production of implant-supported dental restorations, based on the analysis of results obtained using different impression methods, materials, and parallel and angulated implants. The study findings indicate that all aforementioned factors impact the accuracy of the definitive working model. Specifically, 20° implant angulation in relation to the vertical plane has a greater impact on the impression accuracy compared to parallel implants. The open and splint method in combination with addition silicone, as well as the splint method and polyether combination yielded more accurate results when using implants under 20° angulation compared to other method and material combinations. The splint method in combination with addition silicone resulted in the smallest mean deviations from the center of the parallel implant base compared to other combinations of methods and materials. Analysis results further revealed statistically significant differences in the measured indicators across impression methods, implants, and polymer materials.

As the mechanical properties of resin-based dental composite materials are highly relevant in clinical practice, diverse strategies for their potential enhancement have been proposed in the extant literature, aiming to facilitate their reliable use in dental medicine. In this context, the focus is primarily given to the mechanical properties with the greatest influence on clinical success, i.e., the longevity of the filling in the patient’s mouth and its ability to withstand very strong masticatory forces. Guided by these objectives, the goal of the present study was to ascertain whether the reinforcement of dental composite resins with electrospun polyamide (PA) nanofibers would improve the mechanical strength of dental restoration materials. For this purpose, light-cure dental composite resins were interspersed with one and two layers comprising PA nanofibers in order to investigate the influence of such reinforcement on the mechanical properties of the resulting hybrid resins. One set of the obtained samples was investigated as prepared, while another set was immersed in artificial saliva for 14 days and was subsequently subjected to the same set of analyses, namely Fourier-transform infrared spectroscopy (FTIR), scanning electron microscopy (SEM), and differential scanning calorimetry (DSC). Findings yielded by the FTIR analysis confirmed the structure of the produced dental composite resin material. They also provided evidence that, while the presence of PA nanofibers did not influence the curing process, it strengthened the dental composite resin. Moreover, flexural strength measurements revealed that the inclusion of a 16 μm-thick PA nanolayer enabled the dental composite resin to withstand a load of 3.2 MPa. These findings were supported by the SEM results, which further indicated that immersing the resin in saline solution resulted in a more compact composite material structure. Finally, DSC results indicated that as-prepared as well as saline-treated reinforced samples had a lower glass transition temperature (Tg) compared to pure resin. Specifically, while pure resin had a Tg of 61.6 °C, each additional PA nanolayer decreased the Tg by about 2 °C, while the further reduction was obtained when samples were immersed in saline for 14 days. These results show that electrospinning is a facile method for producing different nanofibers that can be incorporated into resin-based dental composite materials to modify their mechanical properties. Moreover, while their inclusion strengthens the resin-based dental composite materials, it does not affect the course and outcome of the polymerization reaction, which is an important factor for their use in clinical practice.