Starch-based biodegradable films have been studied for a long time. To improve starch properties and to increase film characteristics, starch is commonly modified. Amongst different types of starch modifications, oxidation and heat moisture treatment are interesting to explore. Unfortunately, review on these modifications for film application is rarely found, although these starch modifications provide interesting results regarding the starch and film properties. This paper aims to discuss the progress of research on oxidized and heat moisture-treated-starch for edible film application. In general, both HMT and oxidation modification on starch lead to an increase in film’s tensile strength and Young’s modulus, suggesting an improvement in film mechanical properties. The elongation, however, tends to decrease in oxidized starch-based film, hence more brittle film. Meanwhile, HMT tends to result in a more ductile film. The drawback of HMT film is its lower transparency, while the opposite is observed in oxidized films. The observation on WVP (water vapor permeability) of HMT starch-based film shows that the trend of WVP is not consistent. Similarly, an inconsistent trend of WVP is also found in oxidized starch films. This suggests that the WVP parameter is very sensitive to intrinsic and extrinsic factors. Starch source and its concentration in film, film thickness, RH (relative humidity) of film storage, oxidation method and its severity, plasticizer type and its concentration in film, and crystallinity value may partly play roles in determining film properties.