The medical sector is one of the biggest consumers of single-use materials, and while the insurance of sterile media is non-negotiable, the environmental aspect is a chronic problem. Nanocellulose (NC) is one of the safest and most promising materials that can be used in medical applications due to its valuable properties like biocompatibility and biodegradability, along with its good mechanical properties and high water uptake capacity. However, NC has no bactericidal activity, which is a critical need for the effective prevention of infections in chronic diabetic wound dressing applications. Therefore, in this work, a natural product, propolis extract (PE), was used as an antibacterial agent, in different amounts, together with NC to obtain sponge-like structures (NC/PE). The scanning electron microscope (SEM) images showed well-impregnated cellulose fibers and a more compact structure with the addition of PE. According to the thermogravimetric analysis (TGA), the samples containing PE underwent thermal degradation before the unmodified NC due to the presence of volatile compounds in the extract. However, the peak degradation temperature in the first derivative thermogravimetric curves was higher for all the sponges containing PE when compared to the unmodified NC. The antibacterial efficacy of the samples was tested against Staphylococcus aureus, Pseudomonas aeruginosa, and Escherichia coli, as well as on two clinically resistant isolates. The samples completely inhibited the development of Staphylococcus aureus, and Pseudomonas aeruginosa was partially inhibited, while Escherichia coli was resistant to the PE action. Considering the physical and biological properties along with the environmental and economic benefits, the development of an NC/PE wound dressing seems promising.

Cellulose is a versatile biopolymer increasingly applied in medicine and industry due to its biodegradability and biocompatibility, along with the renewability and large availability of source materials. However, finding simple, eco-friendly, and effective methods to modify cellulose to provide it with new functionalities remains a challenge. This work presents a new, inexpensive, and eco-friendly method to chemically modify microcrystalline cellulose (MCC) by the submerged cold plasma treatment of an aqueous suspension of MCC containing different oxidizing agents, such as hydrogen peroxide (H₂O₂), sodium hypochlorite (NaClO), or sodium periodate (NaIO₄). Fourier-transform Infrared (FTIR) and X-ray photoelectron spectroscopy (XPS) showed that plasma treatment intensified the oxidizing effect of H₂O₂, NaClO, and NaIO₄, with plasma-assisted NaClO treatment yielding the highest MCC oxidation level. XPS indicated that the plasma-assisted oxidations also resulted in different degrees of chemical degradation of MCC, a finding further supported by the thermogravimetric analysis (TGA) results. X-ray diffraction (XRD) data revealed a different effect of the oxidizing agents on the crystalline and amorphous regions in MCC. Scanning electron microscopy (SEM) images showed that the combined treatment with plasma and chemical oxidizing agents led to MCC fragmentation and varying degrees of defibrillation into nanofibers.

Poly (3-hydroxybutyrate) (PHB) is a valuable biopolymer that is produced in industrial quantity but is not widely used in applications due to some drawbacks. The addition of cellulose nanofibers (CNF) as a biofiller in PHB/CNF nanocomposites may improve PHB properties and enlarge its application field. In this work, n-octyltriethoxy silane (OTES), a medium-chain-length alkyl silane, was used to surface chemically modify the CNF (CNF_OTES) to enhance their hydrophobicity and improve their compatibility with PHB. The surface functionalization of CNF and nanodimension were emphasized by Fourier transform infrared spectroscopy, X-ray photoelectron spectroscopy, thermogravimetric analysis, atomic force microscopy, dynamic light scattering, and water contact angle (CA). Surface modification of CNF with OTES led to an increase in thermal stability by 25 °C and more than the doubling of CA. As a result of the higher surface hydrophobicity, the CNF_OTES were more homogeneously dispersed in PHB than unmodified CNF, leading to a PHB nanocomposite with better thermal and mechanical properties. Thus, an increase by 122% of the storage modulus at 25 °C, a slight increase in crystallinity, a better melting processability, and good thermal stability were obtained after reinforcing PHB with CNF_OTES, paving the way for increasing PHB applicability.

Nanocellulose (NC) is a valuable material in tissue engineering, wound dressing, and drug delivery, but its lack of antimicrobial activity is a major drawback for these applications. In this work, basil ethanolic extract (BE) and basil seed mucilage (BSM) were used to endow nanocellulose with antibacterial activity. NC/BE and NC/BE/BSM sponges were obtained from nanocellulose suspensions and different amounts of BE and BSM after freeze-drying. Regardless of the BE or BSM content, the sponges started to decompose at a lower temperature due to the presence of highly volatile active compounds in BE. A SEM investigation revealed an opened-cell structure and nanofibrillar morphology for all the sponges, while highly impregnated nanofibers were observed by SEM in NC/BE sponges with higher amounts of BE. A quantitative evaluation of the porous morphology by microcomputer tomography showed that the open porosity of the sponges varied between 70% and 82%, being lower in the sponges with higher BE/BSM content due to the impregnation of cellulose nanofibers with BE/BSM, which led to smaller pores. The addition of BE increased the specific compression strength of the NC/BE sponges, with a higher amount of BE having a stronger effect. A slight inhibition of S. aureus growth was observed in the NC/BE sponges with a higher amount of BE, and no effect was observed in the unmodified NC. In addition, the NC/BE sponge with the highest amount of BE and the best antibacterial effect in the series showed no cytotoxic effect and did not interfere with the normal development of the L929 cell line, similar to the unmodified NC. This work uses a simple, straightforward method to obtain highly porous nanocellulose structures containing antibacterial basil extract for use in biomedical applications.

The growing interest in materials derived from biomass has generated a multitude of solutions for the development of new sustainable materials with low environmental impact. We report here, for the first time, a strategy to obtain bio-based nanocomposites from epoxidized linseed oil (ELO), itaconic acid (IA), and surface-treated nanofibrillated cellulose (NC). The effect of nanofibrillated cellulose functionalized with silane (NC/S) and then grafted with methacrylic acid (NC/SM) on the properties of the resulted bio-based epoxy systems was thoroughly investigated. The differential scanning calorimetry (DSC) results showed that the addition of NCs did not influence the curing process and had a slight impact on the maximum peak temperature. Moreover, the NCs improved the onset degradation temperature of the epoxy-based nanocomposites by more than 30 °C, regardless of their treatment. The most important effect on the mechanical properties of bio-based epoxy nanocomposites, i.e., an increase in the storage modulus by more than 60% at room temperature was observed in the case of NC/SM addition. Therefore, NC’s treatment with silane and methacrylic acid improved the epoxy–nanofiber interface and led to a very good dispersion of the NC/SM in the epoxy network, as observed by the SEM investigation. The dielectric results proved the suitability of the obtained bio-based epoxy/NCs materials as substitutes for petroleum-based thermosets in the fabrication of flexible electronic devices.

In this work, an economically feasible procedure was employed to produce poly (3-hydroxybutyrate-co-3-hydroxyvalerate) (PHBV)-based foams. Thermally expandable microspheres (TESs) were used as a blowing agent, while bacterial cellulose (BC) nanofibers served both as a reinforcing agent and as a means of improving biocompatibility. PHBV was plasticized with acetyltributylcitrate to reduce the processing temperature and ensure the maximum efficiency of the TES agent. The morphological investigation results for plasticized PHBV foams showed well-organized porous structures characterized by a porosity of 65% and the presence of both large pores (>100 µm) and finer ones, with a higher proportion of pores larger than 100 µm being observed in the PHBV nanocomposite containing TESs and BC. The foamed structure allowed an increase in the water absorption capacity of up to 650% as compared to the unfoamed samples. TESs and BC had opposite effects on the thermal stability of the plasticized PHBV, with TESs decreasing the degradation temperature by about 17 °C and BC raising it by 3–4 °C. A similar effect was observed for the melting temperature. Regarding the mechanical properties, the TESs had a flexibilizing effect on plasticized PHBV, while BC nanofibers showed a stiffening effect. An in vitro cytotoxicity test showed that all PHBV compounds exhibited high cell viability. The addition of TESs and BC nanofibers to PHBV biocomposites enabled balanced properties, along with lower costs, making PHBV a more attractive biomaterial for engineering, packaging, or medical device applications.