Filler materials are considered added value (volume) to composite materials. The addition of filler materials leads to altering the material characteristics. Nowadays, there has been a notable increase in bio-based materials in polymers and polymer composites. In this regard, agricultural wastes (low-cost renewable substrates) are used as filler content to prepare bioplastic composites, as they are available plenty in quantity and economical in price. Bioplastics composite samples are compounded by adding different amounts of eggshell powder and walnut shell powder in weight proportion to the plasticized PLA. The plasticization is realized with 5 wt.% of Epoxidized Soybean Oil. The prepared bioplastic granules are further processed by injection molding to dog bone-shaped samples subjected to different mechanical, thermal, and optical microscopy tests. Mechanical tests such as Tensile, Charpy Impact, and Flexural tests yielded decreased properties compared to virgin PLA. However, the properties of plasticized PLA–ES composite showed better results than plasticized PLA–WS composite.

Plastic is being used increasingly in daily life. Most of it is not recyclable, and the remaining plastic cannot be used or decomposed. This causes increased plastic waste, contributing to global warming due to thermal recycling. The major objective of this research was to utilise the maximum plastic waste possible to manufacture bricks that compete with the properties of conventional bricks without affecting the environment and the ecological balance. A balanced mixture of high-density polyethylene (HDPE), quartz sand, and some additive materials, such as bitumen, was used to produce these bricks. Various tests were performed to assess the bricks’ quality, such as compression, water absorption, and efflorescence tests. These bricks had a compression strength of 37.5 MPa, which is exceptionally strong compared to conventional bricks. The efflorescence and water absorption tests showed that the bricks were nearly devoid of alkalis and absorbed almost no water. The obtained bricks were light in weight and cost-effective compared to conventional bricks.

The growing demand for sustainable materials has driven interest in natural fiber-reinforced composites as eco-friendly alternatives to synthetic materials. This research investigates the fabrication and mechanical performance of hemp and sisal fiber-reinforced composites, with a focus on improving fiber–matrix bonding through alkali and fungal treatments. Experimental results show that fungal treatment significantly improves tensile and flexural strength, while hardness slightly decreases. Water absorption tests revealed moderate reductions in hydrophilicity compared to untreated samples, although absolute water uptake remains higher than conventional glass/epoxy composites. Microscopy analysis further confirmed enhanced fiber adhesion and structural integrity in treated specimens. These findings suggest that hybrid composites reinforced with hemp and sisal, particularly with fungal treatment, hold promise for low-to-medium load sustainable applications in the automotive interiors, packaging, and construction industries, where moderate mechanical performance and partial biodegradability are acceptable. This research contributes to the advancement of bio-based composite materials while acknowledging current limitations in long-term durability and complete biodegradability.

Contrary to other polymer processing methods, additive manufacturing processes do not require any pressure during the consolidation of layers. This study investigates the effect of high ambient pressure on the consolidation of layers during the FDM process and their analysis of mechanical properties. An experimental setup was arranged, consisting of a 3D printer integrated into a customized Autoclave, to achieve high strength properties for 3D printed parts as like injection-molded specimens. The autoclave can maintain 135 bar of pressure and a maximum temperature of 185 °C. 3D printing with PLA was carried out at 0 bar, 5 bar, and 10 bar. Tensile, flexural, and Charpy tests were conducted on printed specimens, and the effect of pressure and temperature on 3D-printed samples were analyzed. It could be shown that autoclave preheating before printing and autoclave pressure during printing improves the consolidation of layers immensely. The pressure inside the autoclave provokes a more intimate contact between the layer surfaces and results in higher mechanical properties such as yield strength, Young’s modulus, and impact strength. The properties could be raised 100%.