The formation of polyene-polyyne-based nanocomposites by dehydrohalogenation of the drop-cast-deposited polyvinylidene fluoride, assessment and ion-induced tailoring of their gas sensing properties are reported. The investigated structure was analyzed by scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy, transmission electron microscopy and Fourier-transform infrared spectroscopy, revealing the thickness-dependent incomplete dehydrofluorination of the structure and its porosity induced by KOH treatment. The polyene-polyyne structures modified by low-energy Ar⁺ were studied by SEM and Raman spectroscopy, which showed the morphology variation, the shortening of chains and the graphitization of samples. The resistive gas sensing properties of the samples were analyzed at room temperature, revealing selective sensing of ammonia vapor by non-irradiated sample and the enhancement of the sensing properties for ethanol and water vapor after ion irradiation. With the ion dose enlargement, the change in the sensing response from electrical conductivity increase to decrease was observed for ammonia and ethanol, allowing us to discuss the origin and tunability of the sensing mechanism of the samples.

We report on the formation of the field-effect transistor based on a polyyne–polyene structure. Polyvinylidene chloride (PVDC) drop casting and its subsequent dehydrochlorination in KOH solution allowed for the formation of porous polyyne–polyene material, which was analyzed via transmission electron microscopy, Fourier-transform infrared spectroscopy, and Raman spectroscopy, revealing the presence of sp- and sp²-hybridized chained fragments in the structure. The polyyne–polyene-based field-effect transistor showed a transconductance of 3.2 nA/V and a threshold voltage of −0.3 V. The obtained results indicate that polyyne–polyene-based transistors can be used as discrete elements of molecular electronics and that subsequent studies can be aimed toward the development of selective polyyne–polyene-based gas sensors with tunable sensitivity.

Resistive sensing responses of the thin films obtained by dehydrohalogenation of polyvinylidene chloride (PVDC) and polyvinylidene chloride–polyvinyl chloride (PVDC-PVC) copolymer were investigated. The structure of the samples was studied by transmission electron microscopy, Fourier-transform infrared spectroscopy and Raman spectroscopy. The analyses demonstrate the formation of a porous structure based on polyyne–polyene chains. The formation of a foam-like oxidized sp-rich structure was observed for the samples obtained via the chemical treatment of the PVDC. However, a loose film with a developed structure and a lower fraction of sp-hybridized carbon was observed for KOH-treated PVDC-PVC. The resistive sensing responses of both of the dehydrohalogenated structures were measured for various concentrations of acetone, acetic acid, ammonia hydroxide, methanol, ethanol, benzene and water. The interplay between the efficiency of the dehydrohalogenation of the films, their structure and sensing selectivity is discussed.