Hollow nanostructures are ranked among the top materials for applications in various modern technological areas including energy storage devices, catalyst, optics and sensors. The last years have witnessed increasing interest in the Kirkendall effect as a versatile route to fabricate hollow nanostructures with different shapes, compositions and functionalities. Although the conversion chemistry of nanostructures from solid to hollow has reached a very advanced maturity, there is still much to be discovered and learned on this effect. Here, the recent progress on the use of the Kirkendall effect to synthesize hollow nanospheres and nanotubes is reviewed with a special emphasis on the fundamental mechanisms occurring during such a conversion process. The discussion includes the oxidation of metal nanostructures (i.e., nanospheres and nanowires), which is an important process involving the Kirkendall effect. For nanospheres, the symmetrical and the asymmetrical mechanisms are both reviewed and compared on the basis of recent reports in the literature. For nanotubes, in addition to a summary of the conversion processes, the unusual effects observed in some particular cases (e.g., formation of segmented or bamboo-like nanotubes) are summarized and discussed. Finally, we conclude with a summary, where the prospective future direction of this research field is discussed.

Nanoporous materials are of great importance for a broad range of applications including catalysis, optical sensors and water filtration. Although several approaches already exist for the creation of nanoporous materials, the race for the development of versatile methods, more suitable for the nanoelectronics industry, is still ongoing. In this communication we report for the first time on the possibility of generating nanoporosity in silver nanocolumns using a dry approach based on the oxidation of silver by direct exposure to a commercially available radio-frequency air plasma. The silver nanocolumns are created by glancing angle deposition using magnetron sputtering of a silver target in pure argon plasma. We show that upon exposure to the rf air plasma, the nanocolumns transform from solid silver into nanoporous silver oxide. We further show that by tuning the plasma pressure and the exposure duration, the oxidation process can be finely adjusted allowing for precisely controlling the morphology and the nanoporosity of the silver oxide nanocolumns. The generation of porosity within the silver nanocolumns is explained according to a cracking-induced oxidation mechanism based on two repeated events occurring alternately during the oxidation process: (i) oxidation of silver upon exposure to the air plasma and (ii) generation of nanocracks and blisters within the oxide layer due to the high internal stress generated within the material during oxidation.

In this work, we report on an efficient approach to fabricating large-area and uniform planar arrays of highly ordered nanoporous gold nanowires. The approach consists in dealloying Au–Ag alloy nanowires in concentrated nitric acid. The Au–Ag alloy nanowires were obtained by thermal annealing at 800 °C for 2 h of Au/Ag stacked nanoribbons prepared by subsequent evaporation of silver and gold through a nanograted photoresist layer serving as a mask for a lift-off process. Laser interference lithography was employed for the nanopatterning of the photoresist layer to create the large-area nanostructured mask. The result shows that for a low Au-to-Ag ratio of 1, the nanowires tend to cracks during the dealloying due to the internal residual stress generated during the dealloying process, whereas the increase of the Au-to-Ag ratio to 3 can overcome the drawback and successfully leads to the obtainment of an array of highly ordered nanoporous gold nanowires. Nanoporous gold nanowires with such well-regulated organization on a wafer-scale planar substrate are of great significance in many applications including sensors and actuators.