We have discovered and clarified the ultrahigh glass-forming ability of the metal-organic frameworks—ZIF-62 [Zn(Im _{2− x} bIm _x )].

Stable emission in glass: Lead halide perovskites can exhibit bright, narrow band photoluminescence but have stability issues related to formation of inactive phases and the loss of lead ions. Hou et al . show that the black, photoactive phase of cesium lead iodide can be stabilized by forming a composite with a glassy phase of a metal-organic framework through liquid-phase sintering. The photoluminescence is at least two orders of magnitude greater than that of the pure perovskite. The glass stabilizes the perovskite under high laser excitation, and about 80% of the photoluminescence was maintained after 10,000 hours of water immersion. —PDS

To date, only several microporous, and even fewer nanoporous, glasses have been produced, always via post synthesis acid treatment of phase separated dense materials, e.g. Vycor glass. In contrast, high internal surface areas are readily achieved in crystalline materials, such as metal-organic frameworks (MOFs). It has recently been discovered that a new family of melt quenched glasses can be produced from MOFs, though they have thus far lacked the accessible and intrinsic porosity of their crystalline precursors. Here, we report the first glasses that are permanently and reversibly porous toward incoming gases, without post-synthetic treatment. We characterize the structure of these glasses using a range of experimental techniques, and demonstrate pores in the range of 4 – 8 Å. The discovery of MOF glasses with permanent accessible porosity reveals a new category of porous glass materials that are elevated beyond conventional inorganic and organic porous glasses by their diversity and tunability.