An antibacterial carbon fiber-reinforced plastics (CFRP) was manufactured based on a vitrimer containing imine groups. A liquid curing agent was prepared to include an imine group in the matrix, and was synthesized without a simple mixing reaction and any purification process. The vitrimer used as the matrix for CFRP was prepared by reacting a commercial epoxy with a synthesized curing agent. The structural and thermal properties of the vitrimer were determined by Fourier transform-infrared spectroscopy (FT-IR), differential scanning calorimetry (DSC) and thermogravimetric analysis (TGA). In addition, the temperature-dependent behavior of the vitrimer was characterized by stress relaxation, reshaping, and shape memory experiments. The mechanical properties of composites fabricated using vitrimer were fully analyzed by tensile, flexural, short-beam strength, and Izod impact tests and had mechanical properties similar to reference material. Moreover, both the vitrimer and the vitrimer composites showed excellent antibacterial activity against Staphylococcus aureus and Escherichia coil due to the imine group inside the vitrimer. Therefore, vitrimer composites have potential for applications requiring antimicrobial properties, such as medical devices.

Cross-linked membranes for polymer electrolyte membrane fuel cell application are prepared using highly sulfonated poly(arylene ether sulfone) (SPAES) and polymeric cross-linkers having different hydrophilicities by facile in-situ casting and heating processes. From the advantage of the cross-linked structures made with the use of polymeric cross-linkers, a stable membrane can be obtained even though the polymer matrix with a very high degree of sulfonation was used. In particular, hydrophilic cross-linker is found to be effective in improving physicochemical properties of the cross-linked membranes and at the same time showing reasonable proton conductivity. Accordingly, membrane electrode assembly made from the cross-linked membrane prepared by using hydrophilic polymeric cross-linker exhibits outstanding cell performance under high temperature and low relative humidity conditions (e.g., maximum power density of 176.4 mW cm⁻² at 120 °C and 40% RH).

Thermosetting materials have limitations in terms of reshaping and recycling due to their irreversible bond structures, leading to significant plastic waste issues. Recently, epoxy vitrimers based on dynamic covalent bond exchange have been introduced as promising alternatives to traditional thermosets. Particularly, they demonstrate significant potential applications in the field of multi‐responsive materials. In this research, a self‐healable and mechano‐responsive vitrimer (EB‐V) is successfully prepared, incorporating epoxide spiropyran beads (ESP beads) derived from citric acid and epoxy derivatives. To enable self‐reporting of cracks through color changes, ESP beads are covalently bonded to the vitrimer via an epoxy‐carboxylic acid reaction. The photochromic properties of EB‐V are demonstrated by color and fluorescence changes, and its tensile strength increased from 2.0 to 6.8 MPa compared to the control sample. Dynamic mechanical analysis confirmed the covalent exchange reaction of the vitrimer, revealing its reconfigurable behavior and stress relaxation at elevated temperatures. Furthermore, EB‐V exhibited exceptional properties, including self‐healing and reprocessability. As a smart material, it holds great promise for a wide range of applications, such as sensors, actuators, 4D printing, and industrial safety diagnostics.