Refractory gold and silver ores present significant challenges because precious metals are encapsulated within sulfide matrices, severely limiting extraction by conventional cyanidation. In this study, a pyritic concentrate from the Bacis Mine (Durango, Mexico) was characterized and subjected to two oxidative pretreatments—roasting and alkaline pressure oxidation—before cyanidation. X-ray diffraction confirmed pyrite to be the dominant phase, with quartz and minor carbonates contributing to the material’s refractory character. Roasting at 550 °C achieved gold and silver extraction of 80% and 70%, respectively, which improved to 89% Au and 74% Ag with the addition of hydrogen peroxide. In contrast, alkaline pressure oxidation at 150 °C and 1 MPa O₂ yielded the highest extraction of 92% for Au and 76% for Ag at 1 h. Thermodynamic analysis using the Fe–S Pourbaix diagram at 80 °C supported these experimental results, showing the destabilization of FeS₂ under oxidizing and moderately alkaline conditions. Overall, this study demonstrates that alkaline pressure oxidation is a technically efficient and environmentally favorable pretreatment for refractory gold ores.

Printed circuit boards (PCBs) are a valuable source of raw materials for metal recycling considering that base metal concentration analyses have confirmed that PCB powders are multimetallic in nature and contain high concentrations of Cu, Zn, Ni, and Fe. Given that minerals are not renewable resources, these metals can be recycled through hydrometallurgical processes. In this study, we determined that 2 M sulfuric acid, 0.55 MPa oxygen pressure, and a temperature of 90 °C represent the optimal conditions for leaching of Cu, Zn, and Ni of PCBs, obtaining the highest observed values of recovery of greater than 90% for Zn and 98% for Cu and Ni. The characterization of PCBs by SEM–EDS analyses showed that plates mainly consist of Cu, Ni, and Zn. PCBs can be seen as a potential secondary resource for the recovery of copper, nickel, and zinc. The best potential and pH conditions for the extraction of Cu, Zn, and Ni were also determined on the basis of thermodynamic diagrams.