Fe-based amorphous alloys have advantages of low iron loss and high effective permeability, which are widely used in sensors and actuators. Power efficiency is one of the most important indicators among power conversion applications. We compared the magnetomechancial power conversion factors of metallic glassy ribbons FeCoSiB (Vitrovac 7600) and FeSiB (Metglas 2605SA1). We investigated the crystallization process under different annealing temperatures and tested the magnetomechancial coupling factors (k) and quality factors (Q) by using resonant and anti-resonant methods. We found that the maximum coupling factor of the annealed Vitrovac ribbons was 23% and the figure of merits k²Q was 4–7; however, the maximum coupling factor of the annealed Metglas ribbons was 73% and the maximum value of k²Q was 16. We can observe that the Metglas 2605SA1 ribbons have higher values of the magnetomechanical power efficiency than those of the Vitrovac 7600 ribbons, which means they are better to be used in subsequent research regarding acoustically driven antennas.

The resonant magnetoelectric (ME) effect of Fe₇₈Si₉B₁₃/Pb(Zr,Ti)O₃ (FeSiB/PZT) composites with a surface-modified Fe₇₈Si₉B₁₃ amorphous alloy has been studied. The surface-modified FeSiB can improve the ME coefficient at the resonant frequency by optimizing the magnetomechancial power conversion efficiency. The maximum ME coefficient of the surface-modified ribbons combined with soft PZT (PZT5) is two-thirds larger than that of the composites with fully amorphous ribbons. Meanwhile, the maximum value of the ME coefficient with surface-modified FeSiB ribbons and hard PZT (PZT8) is one-third higher compared with the fully amorphous composites. In addition, experimental results of magnetomechanical coupling properties of FeSiB/PZT composites with or without piezoelectric layers indicate that the power efficiency of the composites first decreases and then increases with the increase in the number of FeSiB layers. When the surface crystalline FeSiB ribbons are combined with a commercially available hard piezoelectric ceramic plate, the maximum magnetoelectric coupling coefficient of the ME composite reaches 5522 V/(Oe*cm), of which the electromechanical resonant frequency is 23.89 kHz.

Understanding the correlation between magnetomechanical coupling factors (k) and damping factors (Q⁻¹) is a key pathway toward enhancing the magnetomechanical power conversion efficiency in laminated magnetoelectric (ME) composites by manipulating the magnetic and mechanical properties of Fe-based amorphous metals through engineering. The k and Q⁻¹ factors of FeSiB amorphous ribbons annealed in air at different temperatures are investigated. It is found that k and Q⁻¹ factors are affected by both magnetic and elastic properties. The magnetic and elastic properties are characterized in terms of the magnetomechanical power efficiency for low-temperature annealing. The k and Q⁻¹ of FeSiB-based epoxied laminates with different stacking numbers show that a −3 dB bandwidth and Young’s modulus are expressed in terms of the magnetomechanical power efficiency for high lamination stacking.

Understanding of the correlation between the magnetomechancial coupling factors (k) and damping factors (Q^-1) is a key pathway to enhance the magnetomechanical power conversion ef-ficiency in laminated magnetoelectric (ME) composites by engineeringly manipulating the magnetic and mechanical properties of Fe-based amorphous metals. The k and Q^-1 factors of FeSiB amorphous ribbons annealed in air at different temperatures are investigated. It is found that k and Q^-1 factors are affected by both magnetic and elastic properties. The magnetic and elastic properties are equalized in terms of the magnetomechanical power efficiency for the low temperature annealing. The k and Q^-1 of FeSiB-based epoxied laminates with different stacking numbers show that the -3 dB bandwidth and Young’s modulus are equalized in terms of the magnetomechanical power efficiency for the high lamination stacking.