In this paper a numerical investigation of replacement implant for partial hip arthroplasty is presented. The long-term stability of hip implants depends, among other things, on the loads acting across the joint. Forces occurring in vivo can be much greater than the recommended test values, because a typical gait cycle generates forces up to 6–7 times the body weight in the hip joint. A finite element analysis (FEA) was performed using 3-dimensional models to examine the mechanical behaviour of the femoral component at forces ranging from 2.5 to 6.3 kN. This implant design was chosen for numerical analysis because stress concentration in femoral component lead to implant fracture. Results show that the force magnitudes acting on the implant are of interest, and that they can cause implant stress field changes and implant stability problems, which can lead to implant failure

The research represents the ongoing investigation of the welded joints behavior made of low-carbon low-alloyed steel in the presence of different multiple defects. Following the initial experimental and numerical analyses performed on low-grade steel, a set of experiments were performed with specimens made of steel EN 1.0044 (commercial designation S275JR), along with development of new numerical models. Four combinations were made, including defects like undercuts, excess weld metal, misalignment, weld face sagging and incomplete root penetration, considering that these defects are often encountered in practice, and can appear simultaneously. The finite element method (FEM) was used to simulate the experiments. Tensile properties of the HAZ and weld metal were calculated using strain measurements by the digital image correlation (DIC) method. The finite element method (FEM) results were in good agreement with the experimental ones.