A Raman spectroscopic study of Cu ₂ ZnSnS ₄ (CZTS) nanocrystals (NCs) produced by a “green” synthesis in aqueous solutions is reported.

The transformation of the vibrational spectrum of Cu₂Zn(Sn_1−xGe_x)S₄single crystals over the entire composition range (0 ≤x≤ 1) is studied experimentally as well as theoretically.

ZnO nanocrystals doped with Nd, Gd, and Er were synthesized using a soft chemical process in ambient atmosphere. Pseudospherical and hexagonal nanocrystals (NC) of the wurtzite phase with a mean size of (7.4 ± 1.7) nm were obtained. The presence of rare earth (RE) dopants was confirmed by X-ray fluorescence (XRF) spectroscopy. The ZnO nanocrystals exhibited simultaneously narrow excitonic- and broad trap/surface-related photoluminescence (PL), both of which were affected by doping with RE atoms. Doping reduced the total PL intensity, suppressing the excitonic emission by a greater extent than the broad band PL. Also, doping resulted in a blue shift of the trap/surface-related emission, while the energy of the excitonic peak remained unchanged. Resonant Raman spectra additionally confirmed the wurtzite phase of ZnO NCs and revealed a shift of the A₁-LO mode towards lower frequency upon doping that could be caused by the mass effect of RE atoms, point defects, and increases in charge carrier concentration. Fitting of the spectra with Voigt profiles showed better results with two surface optical (SO) phonon modes that were previously theoretically predicted for the wurtzite ZnO phase. The influence of RE doping on PL and Raman spectra can be explained by the incorporation of RE ions into the ZnO nanostructures, where the dopants act as non-radiative defects.

The synthesis of (Cu,Ag)-Zn-Sn-S (CAZTS) and Ag-Zn-Sn-S (AZTS) nanocrystals (NCs) by means of “green” chemistry in aqueous solution and their detailed characterization by Raman spectroscopy and several complementary techniques are reported. Through a systematic variation of the nominal composition and quantification of the constituent elements in CAZTS and AZTS NCs by X-ray photoemission spectroscopy (XPS), we identified the vibrational Raman and IR fingerprints of both the main AZTS phase and secondary phases of Ag-Zn-S and Ag-Sn-S compounds. The formation of the secondary phases of Ag-S and Ag-Zn-S cannot be avoided entirely for this type of synthesis. The Ag-Zn-S phase, having its bandgap in near infrared range, is the reason for the non-monotonous dependence of the absorption edge of CAZTS NCs on the Ag content, with a trend to redshift even below the bandgaps of bulk AZTS and CZTS. The work function, electron affinity, and ionization potential of the AZTS NCs are derived using photoelectron spectroscopy measurements.

The effect of flash-lamp annealing (FLA) on the re-crystallization of thin films made of colloidal Cu₂ZnSnS₄ nanocrystals (NCs) is investigated by Raman spectroscopy. Unlike similar previous studies of NCs synthesized at high temperatures in organic solvents, NCs in this work, which have diameters as small as 2–6 nm, were synthesized under environmentally friendly conditions in aqueous solution using small molecules as stabilizers. We establish the range of FLA conditions providing an efficient re-crystallization in the thin film of NCs, while preserving their kesterite structure and improving their crystallinity remarkably. The formation of secondary phases at higher FLA power densities, as well as the dependence of the formation on the film thickness are also investigated. Importantly, no inert atmosphere for the FLA treatment of the NCs is required, which makes this technology even more suitable for mass production, in particular for printed thin films on flexible substrates.