Ultrafine-grained pure titanium prepared by equal-channel angular pressing has favorable mechanical performance and does not contain alloy elements that are toxic to the human body. It has potential clinical value in applications such as cardiac valve prostheses, vascular stents, and hip prostheses. To overcome the material’s inherent thrombogenicity, surface-coating modification is a crucial pathway to enhancing blood compatibility. An electrolyte solution of sodium silicate + sodium polyphosphate + calcium acetate and the micro-arc oxidation (MAO) technique were employed for in situ oxidation of an ultrafine-grained pure titanium surface. A porous coating with anatase- and rutile-phase TiO₂ was generated and wettability and blood compatibility were examined. The results showed that, in comparison with ultrafine-grained pure titanium substrate, the MAO coating had a rougher surface, smaller contact angles for distilled water and higher surface energy. MAO modification effectively reduced the hemolysis rate; extended the dynamic coagulation time, prothrombin time (PT), and activated partial thromboplastin time (APTT); reduced the amount of platelet adhesion and the degree of deformation; and enhanced blood compatibility. In particular, the sample with an oxidation time of 9 min possessed the highest surface energy, largest PT and APTT values, smallest hemolysis rate, less platelet adhesion, a lesser degree of deformation, and more favorable blood compatibility. The MAO method can significantly enhance the blood compatibility of ultrafine-grained pure titanium, increasing its potential for practical applications.

Hydrocarbon contamination accumulated on titanium (Ti) implant surfaces during storage and sterilization is unavoidable and difficult to remove. It impairs the bioactivity of implants, restricts initial interactions between implants and the surrounding biological environment, and has become a common challenge for Ti implants. To overcome this problem, sterilization was considered as the final surface modification and a novel method, hydrothermal sterilization (HS), was proposed. Briefly, stored sandpaper-polished Ti specimens were sterilized in a glass container with pure water at 121 °C for 20 min and kept in the same water until utilization. As a control, another group of specimens was sterilized with conventional autoclaving (AC) at 121 °C for 20 min and stored in sterilization pouches after being dried at 60 °C. Compared with AC, HS deposited numerous nano-sized particles on the substrates, reduced the atomic percentage of the surface carbon, and transformed the Ti surface to a super hydrophilic status. HS also increased the attachment rate, spread, proliferation, and the mineralized nodule areas of rat bone marrow-derived osteoblasts. These results suggest that HS enhances the bioactivity of Ti implants for osteoblasts, and that this biofunctionalization was attributed to nanostructure construction, hydrophilic conversion, and the effective removal of hydrocarbons. Hydrothermal sterilization is proposed to be used as a universal sterilization method for all kinds of titanium implants without apatite coating.