Semiconductor quantum dots (QDs) have been demonstrated viable for efficient light emission applications, in particular for the emission of single photons on demand. However, the preparation of QDs emitting photons with predefined and deterministic polarization vectors has proven arduous. Access to linearly polarized photons is essential for various applications. In this report, a novel concept to directly generate linearly-polarized photons is presented. This concept is based on InGaN QDs grown on top of elongated GaN hexagonal pyramids, by which the predefined elongation determines the polarization vectors of the emitted photons from the QDs. This growth scheme should allow fabrication of ultracompact arrays of photon emitters, with a controlled polarization direction for each individual emitter.

${\mathrm{Ga}}^{+}$ ion implantation of chemical-vapor-deposited GaN nanowires (NWs) is studied using a 50-keV ${\mathrm{Ga}}^{+}$ focused ion beam. The role of dynamic annealing (defect-annihilation) is discussed with an emphasis on the fluence-dependent defect structure. Unlike heavy-ion-irradiated epitaxial GaN film, large-scale amorphization is suppressed until a very high fluence of ${\text{2×10}}^{16}\hspace{0.17em}{\mathrm{ions cm}}^{\text{−2}}.$ In contrast to extended-defects as reported for heavy-ion-irradiated epitaxial GaN film, point-defect clusters are identified as major component in irradiated NWs. Enhanced dynamic annealing induced by high diffusivity of mobile point-defects in the confined geometry of NWs is identified as the probable reason for observed differences.