In this study, we examined whether catalysts with many defects have excellent photoactivity. We prepared ZnO nanoplates with varying degrees of defects in a short time of 4 h by varying the crystal growth temperature at 50, 100, 150, and 200 °C under a strong alkali NaOH atmosphere of 4.0 M. During high-temperature preparation of ZnO, crystal defects were reduced and crystallinity was further increased. In crystallized systems over 100 °C, rhombic nanoplates were used to control particle shape and induce growth in only two axes. The PL, Raman, and XPS analyses confirmed the presence of strong oxygen vacancies in all ZnO nanoplates, and the vacancies decreased with increasing crystallization temperatures. Methylene blue (MB) dye was initially fixed at 50 mg/L with a peak decrease in absorption at 600–700 nm, confirming its decomposition over time. For the 5 h reaction, the MB removal concentration follows the following order: ZnO-50 < ZnO-100 < ZnO-150 < ZnO-200. The study confirms that ZnO-200 nanoplates with fewer oxygen vacancies decompose MB more quickly. ZnO-200 nanoplates synthesized at 200 °C provided the best sterilization performance when tested against gram-positives and gram-negatives, Escherichia coli and Staphylococcus aureus, respectively. ZnO-200 nanoplates after 3 h showed a high sterilization performance of 96.95% (86.67% in a dark room) for staphylococcus aureus and 95.82% (74.66% in a dark room) for Escherichia coli when irradiated with light. Particularly noteworthy in this study is that ·OH and ·O²⁻ radicals are generated more strongly in ZnO-200 than in ZnO-50 nanoplates. These results show that too-strong oxygen vacancies rather inhibit the antibacterial performance, and that the virtue of moderation also exists in the catalytic activity.

The purpose of this study was to evaluate the surface properties of ZnO nanomaterials based on their ability to photodegrade methyl blue dye (MB) and to show their antibacterial properties against different types of Gram-positive bacteria (Bacillus manliponensis, Micrococcus luteus, Staphylococcus aureus) and Gram-negative bacteria (Escherichia coli). In this study, ZnO nanomaterials were synthesized rapidly and easily in the presence of 1–4 M NaOH at a low temperature of 40 °C within 4 h. It was found that the ZnO nanomaterials obtained from the 1.0 M (ZnO–1M) and 2.0 M (ZnO–2M) aqueous solutions of NaOH had spherical and needle-shaped forms, respectively. As the concentration of NaOH increased, needle thickness increased and the particles became rod-like. Although the ZnO nanomaterial shapes were different, the bandgap size remained almost unchanged. However, as the NaOH concentration increased, the energy position of the conduction band shifted upward. Photo current curves and photoluminescence intensities suggested that the recombination between photoexcited electrons and holes was low in the ZnO–4M materials prepared in 4.0 M NaOH solution; however, charge transfer was easy. ∙O₂⁻ radicals were generated more than ∙OH radicals in ZnO–4M particles, showing stronger antibacterial activity against both Gram-positive and Gram-negative bacteria and stronger decomposition ability on MB dye. The results of this study suggest that on the ZnO nanomaterial surface, ∙O₂⁻ radicals generated are more critical for antibacterial activity than particle shape.