To explore the basic mechanical properties and size effects of recycled aggregate concrete (RAC) with different substitution ratios of coarse recycled concrete aggregates (CRCAs) to replace natural coarse aggregates (NCA), the failure modes and mechanical parameters of RAC under different loading conditions including compression, splitting tensile resistance and direct shear were compared and analyzed. The conclusions drawn are as follows: the failure mechanisms of concrete with different substitution ratios of CRCAs are similar; with the increase in substitution ratio, the peak compressive stress and peak tensile stress of RAC decrease gradually, the splitting limit displacement decreases, and the splitting tensile modulus slightly increases; with the increase in the concrete cube’s side length, the peak compressive stress of RAC declines gradually, but the integrity after compression is gradually improved; and the increase in the substitution ratio of the recycled aggregate reduces the impact of the size effect on the peak compressive stress of RAC. Furthermore, an influence equation of the coupling effect of the substitution ratio and size effect on the peak compressive stress of RAC was quantitatively established. The research results are of great significance for the engineering application of RAC and the strength selection of RAC structure design.

This study focuses on the chloride ion penetration resistance of a magnesium phosphate cement (MPC)-based composite material coating on the surface of silicate material. By means of electrical flux method and electric acceleration corrosion tests, the anti-chlorine ion permeation and reinforcement properties of MPC-based materials and Portland cement (OPC) mortar were compared and analyzed. The experimental results show that the electrical flux of the hardened body of the MPC-based material is much lower than that of the Portland cement mortar, and the electrical flux of the hardened body of the MPC mortar can be obviously reduced by adding silica-fume (SF) and fly ash (FA), which, when combined in a suitable proportion, will make the MPC’s hardened body more dense and impermeable. The addition of short cut fibers increases the number of pores, the pore size, and the electrical flux of the cement mortar’s hardened body. The adverse effects of the three fibers on the permeability of the MPC mortar against chlorine ions were as follows: polyvinyl alcohol fiber > glass fiber > basalt fiber. The electrical flux of MPC mortar or MPC paste coated on the surface of the OPC mortar was greatly reduced. Compared with silicate mortar, the MPC-based material has excellent protective performance under the condition of accelerated corrosion.