Decorating Cu ₂ O nanooctahedra with small Au nanograins is a superior strategy to utilize photogenerated charge carriers without generating hot electrons. Photocatalytic activity in these heteronanoparticles is improved even upon low-power excitation.

Integrating more than one type of metal into a nanoparticle that has a well‐defined morphology and composition expands the functionalities of nanocatalysts. For a metal core/porous multimetallic shell nanoparticle, the availability of catalytically active surface sites and molecular mass transport can be enhanced, and the multielemental synergy can facilitate intraparticle charge transport. In this work, a reliable and robust synthesis of such a functional tetrametallic nanoparticle type is presented, where a micro‐ and mesoporous PdPtIr shell is grown on Au nanorods. The effect of critical synthesis parameters, namely temperature and the addition of HCl are investigated on the hydrodynamic size of the micellar pore template as well as on the stability of the metal chloride complexes and various elemental analysis techniques prove composition of the porous multimetallic shell. Due to the synergistic properties, the tetrametallic nanorods possess extensive negative surface charge making them a promising catalyst in reduction reactions. Dye degradation as well as the conversion of p‐nitrophenol to p‐aminophenol is catalyzed by the supportless nanorods without light illumination. By depositing the particles onto conductive substrates, the nanostructured electrodes show promising electrocatalytic activity in ethanol oxidation reaction. The nanocatalyst presents excellent morphological stability during all the catalytic test reactions.

Solar radiation is a cheap and abundant energy for water remediation, hydrogen generation by water splitting, and CO₂ reduction. Supported photocatalysts have to be tuned to the pollutants to be eliminated. Spectral engineering may be a handy tool to increase the efficiency or the selectivity of these. Photonic nanoarchitectures of biological origin with hierarchical organization from nanometers to centimeters are candidates for such applications. We used the blue wing surface of laboratory-reared male Polyommatus icarus butterflies in combination with atomic layer deposition (ALD) of conformal ZnO coating and octahedral Cu₂O nanoparticles (NP) to explore the possibilities of engineering the optical and catalytic properties of hybrid photonic nanoarchitectures. The samples were characterized by UV-Vis spectroscopy and optical and scanning electron microscopy. Their photocatalytic performance was benchmarked by comparing the initial decomposition rates of rhodamine B. Cu₂O NPs alone or on the butterfly wings, covered by a 5 nm thick layer of ZnO, showed poor performance. Butterfly wings, or ZnO coated butterfly wings with 15 nm ALD layer showed a 3 to 3.5 times enhancement as compared to bare glass. The best performance of almost 4.3 times increase was obtained for the wings conformally coated with 15 nm ZnO, deposited with Cu₂O NPs, followed by conformal coating with an additional 5 nm of ZnO by ALD. This enhanced efficiency is associated with slow light effects on the red edge of the reflectance maximum of the photonic nanoarchitectures and with enhanced carrier separation through the n-type ZnO and the p-type Cu₂O heterojunction. Properly chosen biologic photonic nanoarchitectures in combination with carefully selected photocatalyst(s) can significantly increase the photodegradation of pollutants in water under visible light illumination.

The composition of mixed thiol ligand layer prepared on gold nanoprisms can be fine-tuned by controlling molecule concentration levels and addition sequence.

Colloidal Cu₂O nanoparticles can exhibit both photocatalytic activity under visible light illumination and resonant Mie scattering, but, for their practical application, they have to be immobilized on a substrate. Butterfly wings, with complex hierarchical photonic nanoarchitectures, constitute a promising substrate for the immobilization of nanoparticles and for the tuning of their optical properties. The native wax layer covering the wing scales of Polyommatus icarus butterflies was removed by simple ethanol pretreatment prior to the deposition of Cu₂O nanoparticles, which allowed reproducible deposition on the dorsal blue wing scale nanoarchitectures via drop casting. The samples were investigated by optical and electron microscopy, attenuated total reflectance infrared spectroscopy, UV–visible spectrophotometry, microspectrophotometry, and hyperspectral spectrophotometry. It was found that the Cu₂O nanoparticles integrated well into the photonic nanoarchitecture of the P. icarus wing scales, they exhibited Mie resonance on the glass slides, and the spectral signature of this resonance was absent on Si(100). A novel bio-nanohybrid photonic nanoarchitecture was produced in which the spectral properties of the butterfly wings were tuned by the Cu₂O nanoparticles and their backscattering due to the Mie resonance was suppressed despite the low refractive index of the chitinous substrate.

Cuprous oxide nanoparticles can be prepared with a great morphological control, and their composites with gold nanostructures are intensively studied owing to their catalytic performance. In this study, cuprous oxide shell growth on nanosized prism‐shaped gold nanoparticles is investigated, where the core‐particle morphology does not match the prototypical cubic or octahedral symmetry of the embedding cuprous oxide particle. It is shown that different shell morphology is obtained depending on the reducing agent used for the shell deposition. Strong reducing agent (hydrazine) leads to a multi‐slab‐like coating with smooth facets, while under milder conditions (hydroxylamine) a multi‐grain coating is obtained. Successful realization of time‐dependent spectroscopic and structural investigations indicate that in this latter case cuprous oxide shell growth is initiated site‐selectively, namely in the highly curved regions of the particle, with a higher growth rate around the tips of the nanoprisms. This is supported by correlative single‐nanoparticle spectroscopy/scanning electron microscopy measurements, that allow to establish the connection between the optical properties and the structure of these plasmonic/semiconductor core/shell nanoparticles.