In reinforced concrete (RC) constructions, the beam-column junctions are very sensitive to lateral and vertical loads. In the event of unforeseen earthquake and wind loads, this insufficient joint performance can lead to the failure of the entire structure. Cement industries emit a large amount of greenhouse gases during production, thus contributing to global warming. The nature of cement concrete is fragile. Cement output must be reduced in order to ensure environmental sustainability. Geopolymer concrete (GC), which is a green and low-carbon material, can be used in beam-column joints. M30 grade BBGC was developed and employed in the current study. Alkaline liquids are produced when sodium silicate and sodium hydroxide are mixed at room temperature. The alkaline liquid to fly ash ratio was fixed at 0.5, and the concentration of NaOH was fixed at 8 M. The mechanical properties of the Binary Blended Geopolymer concrete (BBGC), containing fly ash and GGBS, at proportions ranging from 0% to 100%, were investigated. This study was further expanded to examine the behavior of two groups of binary blended geopolymer concrete (BBGC) exterior beam-column joints, with cross sections of 230 mm × 120 mm and 170 mm × 120 mm. The column heights and lengths were both 600 mm under reverse cyclic loads in order to simulate earthquake conditions. The failure mechanism, ductility, energy absorption capacity, initial crack load, ultimate load carrying capacity, and structural performance was evaluated. The test findings showed that BBGC with 20% fly ash and 80% GGBS had the highest compressive strength and split tensile strength. When compared with other beam column joints, those containing 20% fly ash and 80% GGBS performed better under cyclic loading. The test findings imply that GGBS essentially enhances the joint performance of BBGC. The microstructural SEM and EDS studies revealed the reasons behind the improvement in strength of the GGBS fly ash-based Geopolymer concrete.

High-performance concrete (HPC) is obtained by inclusion of mineral admixtures like silica fumes and fly ash to the normal concrete. Consumption of natural materials such as sand, natural aggregates, and limestone produces environmental degradation. Similarly, industrial by-products such as fly ash, silica fume, and ferro slag need to be safely disposed of without negatively impacting the environment. The problem being addressed in this study is the need to develop high-performance concrete (HPC) that is durable and environmentally friendly. In recent years, the use of natural aggregates and ferro slag as partial replacements for traditional aggregates has gained attention as a sustainable alternative in the production of concrete. However, there is limited research on the effect of these materials on the mechanical and durability properties of HPC under varied curing conditions. In this current research, high-performance concrete of M60 grade with partial substitution of coarse aggregate with ferro slag aggregate was formed as per the recommendations of the American Concrete Institute with the inclusion of fly ash and silica fume. Natural coarse aggregate was partly substituted by ferro slag aggregate in proportions from 0% to 40%. Partial substitution of cement was made with 15% of fly ash and 10% of silica fumes. Specimens of normal concrete mix (MF0) and modified ferro slag aggregate concrete mix (MF20, MF30, and MF40) were prepared and subjected to acid test, sulphate test, and alternate wet and drying tests to assess the compressive strength of the concrete mixes. Central composite design (CCD) of RSM modelling was adopted to recommend a regression model to forecast the compressive strength of concrete under wetting drying test, acid test, and sulphate attack. Further, natural aggregate, ferro slag, and duration of curing were considered as basic variables to suggest the model. Regression models for response data were evaluated using analysis of variance (ANOVA) and Pareto charts. The results show that the mix MF30 (30% substitution of natural aggregate by ferro slag aggregate) had higher compressive strength. The residual compressive strength at 270 days under alternate wetting and drying, acid attack, and sulphate attack was obtained as 62 MPa, 62.50 MPa, and 66.50 MPa, respectively. Similarly, the percentage loss of weight was obtained as 12.92%, 12.22%, and 6.60% for alternate wetting and drying, acid attack, and sulphate attack, respectively. The findings of the analysis of variance (ANOVA) indicate that the most significant factors influencing the variables and are natural aggregate, ferro slag, and curing period. The regression models for and are extremely significant, as shown by the ANOVA and Pareto chart analyses.