In this study, nickel alloy powders were consolidated by spark plasma sintering. Experiments were performed between 700 and 750°C temperature range under 50 MPa pressure with holding times from 5 to 10 min. In addition to these main spark plasma sintering parameters three different heating rates ranging from 100 to 235°C min⁻¹ and two different particle size ranges (75–106 μm narrow size distribution and −45 μm wide size distribution) were used for the experiments. After sintering, the sliding wear behaviour of the samples was investigated. The results revealed that the density of the material increased with raising the sintering temperature and holding time. However, heating rate and particle size also played an important role in the densification and these parameters were investigated in detail.

The present study reveals for the first time the dry sliding wear behavior of a powder metallurgical pure titanium alloy (Cp-Ti) modified by shot peening. Cp-Ti samples were manufactured via powder metallurgy, and then their surface and subsurface features were modified using a custom-made, fully automated shot-peening system. The texture isotropy rate and the highest orientation angle of the shot-peened samples were 71.5% and 36°, respectively. The Abbott curves of the shot-peened surfaces revealed that the most common areal roughness value was 5.177 μm, with a frequency of 8.1%. Shot-peened surfaces exhibited an ~20% lower wear rate than unpeened surfaces under dry sliding wear, whereas the coefficient of friction was the same for both surfaces. Micro-ploughing, micro-cutting, oxidation, and three-body abrasion wear mechanisms were observed on the shot-peened and unpeened surfaces. High resolution 3D surface topographies of worn unpeened and shot-peened surfaces revealed micro-scratches and inhomogeneities along wear tracks, which are indicative of three-body abrasion mechanisms during contact. In addition, vertical and horizontal microcracks were visible just beneath the wear track, suggesting a clear indication of plastic deformation during contact. The cross-sectional hardness maps of shot-peened samples revealed the formation of a work-hardened surface layer with shot peening, which improved the wear resistance. These findings support that shot peening can be a useful tool to modify the surface and tribological properties of powder metallurgical Cp-Ti alloys.