The materials with grain size gradient variation on the surface, which were prepared with mechanical-induced severe plastic deformation, always show high resistance to high and low cycle fatigue and frictional wear because of their good strength–ductility synergy. The ultrasonic surface rolling treatment (USRT) has the advantages of high processing efficiency, good surface quality, and large residual compressive stress introduced to the surface after treatment. The USRT was used to prepare aluminum alloy (AA7075) samples with a surface gradient structure; meanwhile, the microstructural evolution mechanism of the deformation layers on the gradient structure was studied with XRD, SEM, and TEM. The microstructure with gradient distribution of grain size and dislocation density formed on the surface of AA7075 aluminum alloy after USRT. The surface layer consists of nanocrystals with random orientation distribution, and high-density dislocation cells and subgrains formed in some grains in the subsurface layer, while the center of the material is an undeformed coarse-grained matrix. The results show that the dislocation slip dominates the grain refinement process, following the continuous cutting and refinement of dislocation cells, subgrains, and fragmentation of the second precipitates. This study systematically clarified the mechanism of grain refinement and nanocrystallization on the surface of high-strength aluminum alloys and laid a theoretical foundation for further research on mechanical behavior and surface friction and wear properties of high-strength non-ferrous materials with gradient structure.

TiC-reinforced AZ91D magnesium alloy composites were synthesized through the in situ reaction between an AZ91D melt and Ti-C-Al preforms. The microstructural evolution characteristics and phase transformation were investigated at different melt reaction temperatures (1013, 1033, and 1053 K), with the aim of understanding the in situ formation mechanism of TiC particles from thermodynamic and kinetic perspectives. The results showed that the temperature played a critical role in determining the formation and morphology of TiC. Initially, only the Al₃Ti phase was formed through the reaction between Ti and Al when the temperature was 1013 K. With the increase in the melt temperature, the A1₃Ti’s thermodynamic stability decreased, and dissolution and precipitation reactions occurred at higher temperatures (1033 and 1053 K, respectively), contributing to the formation of TiC particles. The formation of the TiC phase was attributed to two factors: Firstly, A1₃Ti as an intermediate product reacted with carbon and formed TiC with increasing temperature. Secondly, the in situ TiC reaction was promoted due to the increased reaction-driving force provided by the increasing temperature.