One method of treating diabetic foot ulcers, mainly superficial and deep ulcers, is using a wound dressing in the form of a hydrogel. Sericin derived from silkworm cocoons is a promising hydrogel material candidate because it has anti-inflammatory properties and stimulates collagen production. Sericin was combined with PVA to increase the stability of the resulting hydrogel. Sericin/PVA hydrogel was prepared using the freeze–thawing method with variations in the solution concentration and volume ratio of PVA and sericin. Sericin was successfully extracted using an autoclave method. The FTIR results confirmed that sericin extracted from the cocoon had a dominant secondary structure in the form of a β-sheet. Hydrogel with a concentration of 4% with a 1:1 ratio of PVA and sericin showed good stability and resulted in a hydrogel with characteristics that combine PVA and sericin. The resulting hydrogel had an average pore size range of 24–191 µm and a porosity range of 70–85%, which meets the requirements for wound dressings. Through degradation testing in PBS solution, it was found that the sericin/PVA hydrogel experienced degradation of 60–75% after 672 h of testing.

Textile industry waste contains high concentrations of heavy metals such as Pb(II) and Cr(VI) that must be reduced before they are released to the environment. The adsorption method is one way to reduce the heavy metal content. In this work, we develop a porous cellulose nanofiber (CNF) aerogel modified with graphene oxide (GO) as an alternative aerogel adsorbent for Pb(II) and Cr(VI). Cellulose was extracted from banana peduncle, a biomass waste that remains largely underutilized. The addition of GO aims to increase the adsorption properties. The aerogel adsorbents were synthesized by varying the ultrasonication time to 45 min for CNF 45 and 60 min for CNF 60, and the amount of GO added to 1 mL and 2 mL. The aerogel adsorbents were successfully prepared using the freeze-drying method with CNF45, CNF60, CNF45/GO1, CNF45/GO2, CNF60/GO1, and CNF60/GO2 variations. CNF was successfully isolated from a banana peduncle with an average diameter of 44.16 nm for 45 min (CNF 45) and an average diameter of 14.6 nm for 60 min (CNF 60) of ultrasonication. Chemical treatment and ultrasonication reduced the crystallinity index value of cellulose by 73% and 61% for CNF 45 and CNF 60, respectively. CNF aerogel has a very low shrinkage rate (<7%), resulting in a larger surface area. CNF60/GO2 obtained the optimum adsorption ability for Pb(II) metal at a concentration of 100 ppm and 27.27 mg/g at 30 min. On the other hand, the adsorption ability of Cr(VI) metal was obtained by CNF60/GO2 at a concentration of 100 ppm and 13.48 mg/g at 30 min. SEM images show that all aerogel adsorbents are porous, with a porosity value range of 96–98%. In conclusion, CNF60/GO2 proved to be the most effective aerogel adsorbent, offering the potential for heavy metal removal from industrial wastewater.