We synthesized iron(II)-triazole spin crossover compounds of the type [Fe(atrz)₃]X₂ and incorporated and deposited them on electrospun polymer nanofibers. For this, we used two separate electrospinning methods with the goal of obtaining polymer complex composites with intact switching properties. In view of possible applications, we chose iron(II)-triazole-complexes that are known to exhibit spin crossover close to ambient temperature. Therefore, we used the complexes [Fe(atrz)₃]Cl₂ and [Fe(atrz)₃](2ns)₂ (2ns = 2-Naphthalenesulfonate) and deposited those on fibers of polymethylmethacrylate (PMMA) and incorporated them into core–shell-like PMMA fiber structures. These core–shell structures showed to be inert to outer environmental influences, such as droplets of water, which we purposely cast on the fiber structure, and it did not rinse away the used complex. We analyzed both the complexes and the composites with IR-, UV/Vis, Mössbauer spectroscopy, SQUID magnetometry, as well as SEM and EDX imaging. The analysis via UV/Vis spectroscopy, Mössbauer spectroscopy, and temperature-dependent magnetic measurements with the SQUID magnetometer showed that the spin crossover properties were maintained and were not changed after the electrospinning processes.

Complexes like iron (II)-triazoles exhibit spin crossover behavior at ambient temperature and are often considered for possible application. In previous studies, we implemented complexes of this type into polymer nanofibers and first polymer-based optical waveguide sensor systems. In our current study, we synthesized complexes of this type, implemented them into polymers and obtained composites through drop casting and doctor blading. We present that a certain combination of polymer and complex can lead to composites with high potential for optical devices. For this purpose, we used two different complexes $$[\text {Fe}(\text {atrz})_{3}](2\, \text {ns})2$$[ Fe ( atrz ) 3 ] ( 2 ns ) 2 and $$[\text {Fe}(\text {atrz})_{3}]\text {Cl}_{1.5}(\text {BF}_{4})_{0.5}$$[ Fe ( atrz ) 3 ] Cl 1.5 ( BF 4 ) 0.5 with different polymers for each composite. We show through transmission measurements and UV/VIS spectroscopy that the optical properties of these composite materials can reversibly change due to the spin crossover effect.

Compounds that exhibit the spin crossover effect are known to show a change of spin states through external stimuli. This reversible switching of spin states is accompanied by a change of the properties of the compound. Complexes, like iron (II)-triazole complexes, that exhibit this behavior at ambient temperature are often discussed for potential applications. In previous studies we synthesized iron (II)-triazole complexes and implemented them into electrospun nanofibers. We used Mössbauer spectroscopy in first studies to prove a successful implementation with maintaining spin crossover properties. Further studies from us showed that it is possible to use different electrospinning methods to either do a implementation or a deposition of the synthesized solid SCO material into or onto the polymer nanofibers. We now used a solvent in which both, the used iron (II)-triazole complex [Fe(atrz)₃](2 ns)₂ and three different polymers (Polyacrylonitrile, Polymethylmethacrylate and Polyvinylpyrrolidone), are soluble. This shall lead to a higher homogeneous distribution of the complex along the nanofibers. Mössbauer spectroscopy and other measurements are therefore in use to show a successful implementation without any significant changes to the complex.

We synthesized iron(II)-triazole spin crossover compounds of the type [Fe(atrz)3]X2 and incorporated and deposited them on electrospun polymer nanofibers. In view of possible applications, we chose iron(II)-triazole-complexes that are known to exhibit spin crossover close to ambient temperature. Therefore we used the complexes [Fe(atrz)3]Cl2 and [Fe(atrz)3](2ns)2 (2ns = 2Naphthalenesulfonate) and analyzed them with IR-, UV/Vis and Mossbauer spectroscopy and with a SQUID magnetometer. The synthesized complexes were then in one attempt deposited on fibers of polymethylmethacrylate (PMMA) and in another attempt incorporated into core-shell like PMMA fiber structures. This was done via two different electrospinning methods. Deposition was performed by uniaxial electrospinning and incorporation was performed by coaxial electrospinning. The obtained polymer-complex-composites were then further investitgated by the same methods as the pure complexes as well as by SEM pictures and EDX measurements. The analysis by UV/Vis spectroscopy, Mössbauer spectroscopy and temperature-depended magnetic measurements with the SQUID magnetometer showed that the spin crossover properties were maintained and were not changed after the electrospinning processes and that the complexes were not harmed during the procedure.