Production of actinide oxide powder via dry thermal decomposition of corresponding oxalates is currently carried out on the industrial scale at temperatures exceeding 500 °C. Although it is simple, this method presents some disadvantages such as high decomposition temperature with a direct effect on the surface area, pre-organised morphology of the nanoparticles affecting the sintering behaviour, etc. We have recently proposed the decomposition of An^IV-oxalates under hot compressed water conditions as a straightforward way to produce reactive actinide oxide nanocrystals. This method could be easily applied at low temperatures (95–250 °C) in order to generate highly crystalline nano-AnO₂. We present here the formation conditions of AnO₂ (An = Th, U, Np, and Pu) and some associated solid solutions, their stability, and grain growth during thermal treatment. The involvement of water molecules in the mechanism of the oxalate decomposition under the hot compressed water conditions has been demonstrated by an isotopic exchange reaction during the thermal treatment of the hydrated oxalate in H₂[¹⁷O] through MAS-NMR and Raman techniques.

Here we provide evidence that the formation of PuO₂ nanoparticles from oxidized Pu^VI under alkaline conditions proceeds through the formation of an intermediate Pu^V solid phase, similar to NH₄PuO₂CO₃, which is stable over a period of several months. For the first time, state‐of‐the‐art experiments at Pu M₄ and at L₃ absorption edges combined with theoretical calculations unambiguously allow to determine the oxidation state and the local structure of this intermediate phase.

The hydrothermal decomposition of actinide(IV) oxalates (An= Th, U, Pu) at temperatures between 95 and 250 °C is shown to lead to the production of highly crystalline, reactive actinide oxide nanocrystals (NCs). This aqueous process proved to be quantitative, reproducible and fast (depending on temperature). The NCs obtained were characterised by X-ray diffraction and TEM showing their size to be smaller than 15 nm. Attempts to extend this general approach towards transition metal or lanthanide oxalates failed in the 95–250 °C temperature range. The hydrothermal decomposition of actinide oxalates is therefore a clean, flexible and powerful approach towards NCs of AnO₂ with possible scale-up potential.