Wood-based materials are multifunctional green and environmentally friendly natural construction materials, and are widely used in decorative building materials. For this reason, a lot of research has been carried out to develop new and innovative wood surface improvements and make wood more appealing through features such as fire-retardancy, hydrophobicity, and antibacterial properties. To improve the performance of wood, more and more attention is being paid to the functioning of the surface. Understanding and mastering technology to improve the surface functionality of wood opens up new possibilities for developing multifunctional and high-performance materials. Examples of these techniques are ion crosslinking modification and coating modification. Researchers have been trying to make wooden surfaces more practical for the past century. This study has gradually gained popularity in the field of wood material science over the last 10 years. This paper provides an experimental reference for research on wood surface functionalization and summarizes the most current advancements in hydrophobic, antibacterial, and flame-retardant research on wood surfaces.

The combustibility of wood can be improved by physical and chemical means, thus expanding the use of wood products. In this study, two novel phosphorus-nitrogen flame retardants (UCPR and MCPR) were developed, and the intercalated modified layered double hydroxides (LDH) thereof were designated as UCPR-LDH and MCPR-LDH. By impregnating poplar veneer with UCPR-LDH and MCPR-LDH solutions, the study investigated the effects of different concentrations (1%, 5%, 10%), processes (vacuum-pressure impregnation, room temperature impregnation, normal-pressure impregnation), and impregnation times (2 h, 3 h, 24 h, 48 h) on the weight-gain rate of veneer. The optimal process was then selected for preparing formaldehyde-free three-layer plywood. Nuclear magnetic resonance (NMR) and Fourier transform infrared (FTIR) were used to characterize the UCPR and MCPR. Meanwhile, gel-permeation chromatography (GPC) demonstrated that the molecular weight of the synthesized flame retardants increased as their molecular distribution became more uniform. The impregnation process was performed at normal temperature and pressure for 48 h at a 5% flame retardant concentration. Results from cone calorimetry indicate that the UCPR-LDH plywood exhibits a peak heat release rate that is 30.43% lower than that of the control group, demonstrating superior thermal barrier performance. The smoke emission of the MCPR-LDH plywood was reduced by 33.62% compared to the control group, indicating superior smoke suppression performance. This method presents a viable approach for synthesizing organic-inorganic flame retardants.