In this paper, ordinary Portland cement, ultrafine cement, polyurethane, and epoxy resin were selected as typical grouting materials. Grouting simulation tests were first conducted to prepare the grouted concrete crack sample. The effect of concrete crack parameters (i.e., crack aperture and roughness), grout water–cement ratio, and grouting pressure on the water-plugging performance of different grouting materials was explored through the impermeability test. The microstructure of grouted concrete cracks was analyzed by means of scanning electron microscopy (SEM) and computed tomography (CT), and the difference in water-plugging performance of different grouting materials was explained at the micro level. The results show that the impermeability of the four grouting materials was ranked as follows: Epoxy resin > polyurethane > ultra-fine cement > ordinary Portland cement. The concrete cracks grouted by epoxy resin have the highest plugging failure water pressure and the lowest permeability, which is the optimal grouting material. The effectiveness of crack grouting in water-plugging was directly proportional to the grouting pressure, provided the pressure did not exceed a certain value. When the pressure surpassed the threshold, the increase in pressure did not have a significant impact on the water plugging performance. For the two cement-based materials, the threshold pressure was 1 MPa, while for the other two chemical grouts, it was 2 MPa. The two cement-based grouts with a water–cement ratio of 0.8 showed optimal water-plugging performance. The water-plugging performance of ordinary Portland cement paste, ultra-fine cement pastes, and polyurethane grout was negatively correlated with crack aperture and positively correlated with crack roughness. However, the water-plugging performance of epoxy resin grout was not affected by crack aperture or roughness.

The creep damage behavior of rocks is very important for evaluating the stability and safety of key rock engineering. Based on the Lianhua Tunnel Project in China, this paper aims to study the creep damage mechanics, the influencing factors and the creep constitutive models of sandy shale. In order to achieve these goals, a uniaxial compressive strength test and a creep test under different moisture contents and load levels were carried out. According to the test results, the creep parameters (elastic coefficients E₁ and E₂ and viscosity coefficients η₁ and η₂) of the Burgers Model were achieved, and the relationship between the creep parameters and moisture content, ω, was established accordingly (E₁ = f(ω), E₂ = f(ω), η₁ = f(ω), η₂ = f(ω)). A fully weathered sandy-shale creep constitutive model considering moisture content was finally obtained. Test results showed that creep deformation increases with any increase in load level or moisture content, and the influence of moisture content is more significant. For instance, creep deformation increased by 35% when the load increased by 50%, and creep deformation increased by 82% when the moisture content increased by 45%. In addition, the creep rate in the steady stage and the duration of the primary creep stage increased with any increase in moisture content or load level. The higher the moisture content, the greater the influence of creep deformation on the total deformation. The creep model of fully weathered sandy shale showed that the elastic coefficients (E₁, E₂) and the viscosity coefficients (η₁, η₂) are negatively correlated to moisture content; E₁ is negatively correlated to load level; and E₂, η₁ and η₂ are positively correlated to load level. Qualitative and quantitative analysis of fully weathered sandy shale can improve the existing research of creep properties and is expected to provide theoretical support for treatment of large deformation disasters in the fully weathered sandy-shale stratum.