The current study investigates the variation and physicochemical properties of ambient particulate matter (PM) in the very important location which lies in the foothills of the Hindu Kush ranges in northern Pakistan. This work investigates the mass concentration, mineral content, elemental composition and morphology of PM in three size fractions, i.e., PM₁, PM_2.5 and PM₁₀, during the year of 2019. The collected samples were characterized by microscopic and spectroscopic techniques like Fourier transform infrared spectroscopy, X-ray diffraction spectroscopy and scanning electron microscopy (SEM) coupled with energy-dispersive X-ray (EDX) spectroscopy. During the study period, the average temperature, relative humidity, rainfall and wind speed were found to be 17.9 °C, 65.83%, 73.75 mm and 0.23 m/s, respectively. The results showed that the 24 h average mass concentration of PM₁₀, PM_2.5 and PM₁ were 64 µgm⁻³, 43.9 µgm⁻³ and 22.4 µgm⁻³, respectively. The 24 h concentration of both PM₁₀ and PM_2.5 were 1.42 and 2.92 times greater, respectively, than the WHO limits. This study confirms the presence of minerals such as wollastonite, ammonium sulphate, wustite, illite, kaolinite, augite, crocidolite, calcite, calcium aluminosilicate, hematite, copper sulphate, dolomite, quartz, vaterite, calcium iron oxide, muscovite, gypsum and vermiculite. On the basis of FESEM-EDX analysis, 14 elements (O, C, Al, Si, Mg, Na, K, Ca, Fe, N, Mo, B, S and Cl) and six groups of PM (carbonaceous (45%), sulfate (13%), bioaerosols (8%), aluminosilicates (19%), quartz (10%) and nitrate (3%)) were identified.

In the present study, pure, Co, Gd, and Co/Gd di-doped ZnO nanoparticles were synthesized via the co-precipitation synthesis route. The prepared samples were characterized through different techniques such as the X-ray diffraction method (XRD), scanning electron microscopy (SEM), UV-Vis spectroscopy, photoluminescence (PL)spectroscopy, and an impedance analyzer and vibrating sample magnetometer (VSM). The XRD pattern shows ZnO’s wurtzite hexagonal crystal structure; moreover, the shifting of characteristic peaks toward the lower angle indicates the inclusion of Co and Co/Gd in the ZnO host lattice. SEM micrographs show various morphologies such as rods, the agglomeration of particles, and spherical nanoparticles. The UV-Vis spectroscopy reveals that the absorption increased in the visible region and there was a substantial redshift for the doped samples. The bandgap decreased from 3.34 to 3.18 eV for the doped samples. The PL spectra show near-edge and inter-band transitions; the origin of inter-band transitions is attributed to the defect states present within the bands. The dielectric constant is strongly frequency dependent and decreases with Co and Co/Gd doping, while the electrical conductivity increases. A VSM study indicates that pure ZnO is diamagnetic, while the Co and Co/Gd doped ZnO nanoparticles showed ferromagnetic behavior. Under UV-visible light irradiation, the Co/Gd-ZnO nanoparticles showed higher photocatalytic activity than the ZnO nanoparticles. The enhanced photocatalytic activity may be attributed to a decreased bandgap with doping.