The effects of a new material based on hydroxyapatite and calcium silicates, named ALBO-MPCA, were investigated on the liver, kidney and spleen. The material was administrated orally for 120 days in an in vivo model in Wistar rats, and untreated animals served as a control. Hematological and biochemical blood parameters were analyzed. Qualitative histological analysis of tissues, change in mitotic activity of cells, and histological characteristics was conducted, as well as quantitative stereological analysis of parenchymal cells, blood sinusoids, and connective tissues. Additionally, the protein expressions of Ki67 and CD68 markers were evaluated. Histological analysis revealed no pathological changes after the tested period. It showed the preservation of the architecture of blood sinusoids and epithelial cells and the presence of mitosis. Additionally, the significantly increased number of the Ki67 in the presence of ALBO-MPCA confirmed the proliferative effect of the material noticed by stereological analysis, while immunoreactive CD68 positive cells did not differ between groups. The study showed non-toxicity of the tested material based on the effects on the hematological, biochemical, and observed histological parameters; in addition, it showed evidence of its biocompatibility. These results could be the basis for further steps toward the application of tested materials in endodontics.

Background/Aim. In dentistry, the concept of using inert materials for tissue repair has been replaced by the strategy to find bioactive materials which positively interact with human tissues. The aim of this study was to characterize the physicochemical properties of the commercially available calcium silicate and calcium carbonate-based dental cement, biodentine (Septodont, France). Methods. Material elucidation included the measurements of radiopacity, scanning electron microscopy and x-ray dispersive analyses, wettability, Fourier transform infrared spectroscopy, microindentation, micro- to nanoporosity, setting time, pH and calcium ion release. The cells (mouse bone marrow mesenchymal stem cells ? BMSCs) were grown on biodentine surface in order to evaluate its behaviour under biological conditions. Results. The radiopacity of the cement (2.8 mmAl) was below ISO requirement for a root canal filling material. The cement was composed of fine powder with particles similar in size and shape, changing from oval to cubic after having been soaked in a simulated body fluid. Biodentine demonstrated good micromechanical properties and low porosity attributed to microporosity with the average pore size of 92 ?m. Wettability (contact angle = 41?), calcium ion release (0.098 ?g/cm?) and pH of storage solution (9.07) showed satisfactory characteristics. The BMSCa in intimate contact with cement particles remained viable, indicating biodentine good biocompatibility. Conclusion. Biodentine exhibits good mechanical and physicochemical characteristics, but possesses insufficient radiopacity.