Modern agriculture produces a very large amount of agricultural waste that remains unused. The use as a reinforcer of these renewable resources for the realization of composite materials, and the finding of useful industrial applications, constitutes or provokes the groups of researchers in this field. The study conducted in this article falls in this direction. Composites were fabricated with the chopped wheat straw reinforcement and epoxy resin matrix or hybrid resins with 50% and 70% Dammar volume proportions. Some mechanical properties of this type of composite materials were studied based on tensile strength, SEM analysis, water absorption/loss, vibration behavior and compression strength. The strength–strain and strain–strain diagrams, the modulus of elasticity, the breaking strength and the elongation at break were obtained. Compared to the epoxy resin composition, those with 50 and 70% Dammar, respectively, have a 47 and 55% lower breaking strength and a 30 and 84% higher damping factor, respectively. Because the values of these mechanical properties were limited, and in practice superior properties are needed, sandwich composites were manufactured, with the core of previously studied compositions, to which the outer faces of linen fabric were applied. These composites were applied to the bend (in three points), obtaining the force–deformation diagrams. The obtained properties show that they can be used in construction (paneling, shells, etc.), or in the furniture industry.

The main objective of this study was to manufacture and test environmentally friendly composite materials using biomass residues as reinforcement: pine needles and recovered paper. A mixed matrix was also used, with natural dammar resin as the predominant component, in order to favor the eco-friendly nature of the resulting material. The manufacturing process employed was the lay-up hand technique. Another objective was to investigate how dammar resin influences the mechanical properties as its mass percentage increases in the mixed resin composition. To investigate the influence of dammar resin on the mechanical properties of the composites, additional materials were fabricated for comparison, using the same reinforcements but with two types of synthetic matrices: epoxy and acrylic. The samples were tested for tensile strength, compression, bending, Shore D hardness, and vibrations. The results indicated that as the percentage of dammar in the matrix increased, a decrease in the strength and rigidity of the material occurred, accompanied by an increase in elasticity and ductility. Water absorption tests showed that the saturation process occurred much faster, as pine needles tend not to absorb a significant amount of water due to the presence of lignin, wax, resins, and pectin, which act as a natural water-repellent barrier.

The study focused on the potential use of agricultural waste (corn cob) in the manufacturing of composite materials. In the first stage, composite materials were manufactured and tested using synthetic matrices (epoxy and acrylic) and hybrid matrices based on dammar resin (50% dammar, 60% dammar, and 70% dammar). Since it was observed that the samples had low mechanical properties under tensile and bending loads, the study was expanded to the production of sandwich-type composites with silk fabric facings. It was found that, by utilizing silk fiber, both tensile and bending strength increased from a few hundred percent up to a few thousand percent, compared to the samples that are only reinforced with crushed corn cob.

This study aimed to investigate the influence of dammar resin on the mechanical properties of composite materials reinforced with corn husk and paper waste laminates. Different percentages of dammar resin (50%, 60%, and 70%) were added to the matrix while keeping the reinforcement constant. For all samples, the ratio was maintained at 40% matrix and 60% reinforcement. With the experimental results obtained, statistical analyses were conducted: two-way analysis of variance (ANOVA), Levene’s test, Shapiro-Wilk test, and ANOVA post hoc (with Bonferroni correction). The null hypothesis stated that dammar resin does not influence the mechanical properties. For all tests considered, the null hypothesis was rejected (p < 0.05), the variances were homogeneous (p > 0.05), and the data followed a normal distribution (p > 0.05). It was found that dammar resin had a significant influence on the mechanical properties as the percentage increased from 50% to 70% (p < 0.0083). For each test, based on already known premises, an explanation of the phenomenon that could occur due to the insertion of dammar resin was provided, serving to complement and validate the statistical estimations.