Using the newly designed exciplex-forming 1,2,3-triazole-based acceptors with fast and efficient singlet → triplet intersystem crossing (ISC) processes, carbazole and benzoyl-1H-1,2,3-triazole derivatives were synthesized by Dimroth-type 1,2,3-triazole ring formation and Ullmann–Goldberg C–N coupling reactions. Due to the exciplex formation between covalently bonded electron-donating (carbazole) and 1,2,3-triazole-based electron-accepting moieties with small singlet-triplet splitting (0.07–0.13 eV), the compounds exhibited ISC-assisted bluish–green thermally activated delayed fluorescence. The compounds were characterized by high triplet energy levels ranging from 2.93 to 2.98 eV. The most efficient exciplex-type thermally activated delayed fluorescence was observed for ortho-substituted carbazole-benzoyl-1H-1,2,3-triazole which was selected as a host in the structure of efficient solution-processed white light-emitting diodes. The best device exhibited a maximum power efficiency of 10.7 lm/W, current efficiency of 18.4 cd/A, and quantum efficiency of 7.1%. This device also showed the highest brightness exceeding 10 thousand cd/m². Usage of the exciplex-forming host allowed us to achieve a low turn-on voltage of 3.6 V. High-quality white electroluminescence was obtained with the close to nature white color coordinates (0.31, 0.34) and a color rendering index of 92.

Motivated to minimize the effects of solid-state solvation and conformation disorder on emission properties of donor-acceptor-type emitters, we developed five new asymmetric multiple donor-acceptor type derivatives of tert-butyl carbazole and trifluoromethyl benzene exploiting different electron-accepting anchoring groups. Using this design strategy, for a compound containing four di-tert-butyl carbazole units as donors as well as 5-methyl pyrimidine and trifluoromethyl acceptor moieties, small singlet-triplet splitting of ca. 0.03 eV, reverse intersystem crossing rate of 1 × 10⁶ s^-1, and high photoluminescence quantum yield of neat film of ca. 75% were achieved. This compound was also characterized by the high value of hole and electron mobilities of 8.9 × 10^-4 and 5.8 × 10^-4 cm² V^-1 s^-1 at an electric field of 4.7 × 10⁵ V/cm, showing relatively good hole/electron balance, respectively. Due to the lowest conformational disorder and solid-state solvation effects, this compound demonstrated very similar emission properties (emission colors) in non-doped and differently doped organic light-emitting diodes (OLEDs). The lowest conformational disorder was observed for the compound with the additional accepting moiety inducing steric hindrance, limiting donor-acceptor dihedral rotational freedom. It can be exploited in the multi-donor-acceptor approach, increasing the efficiency. Using an emitter exhibiting the minimized solid-state solvation and conformation disorder effects, the sky blue OLED with the emitting layer of this compound dispersed in host 1,3-bis(N-carbazolyl)benzene displayed an emission peak at 477 nm, high brightness over 39 000 cd/m², and external quantum efficiency up to 15.9% along with a maximum current efficiency of 42.6 cd/A and a maximum power efficiency of 24.1 lm/W.

In contrast to the red electroluminescence emission frequently observed in porphyrins based OLED devices, the present devices exhibit a nearly white emission with greenish yellow, yellowish green and blue green hues in the case of Fe^II(TCPPBr₆) (TCPPBr₆ = β-hexabromo-meso-tetrakis-(4-phenyl carboxyl) porphyrinato), Zn^II(TPPBr₆) and Co^II(TPPBr₆), respectively.