Ti containing Cu-based (TC) alloy reinforced glass-ceramic bond was fabricated for cubic boron nitride (CBN) abrasive tool materials, and its crystal composition, phase transformation, sintering activation energy, microstructure, element diffusion mathematical model, physical properties, and the bonding mechanism between the TC alloy reinforced glass-ceramic bond and the CBN grains were systematically investigated. The results showed that the structure, composition and sintering behavior of glass-ceramic were influenced by TC alloy adding. The generated TiO₂ affected obviously the precipitation of β-quartz solid solution Li₂Al₂Si₃O₁₀, thus improving the relative crystallinity, mechanical strength and thermal properties. By establishing the mathematical model for element diffusion, the element diffusion coefficients of Ti and Cu were 7.82 and 6.98 × 10⁻¹¹ cm²/s, respectively, which indicated that Ti diffused better than Cu in glass-ceramic. Thus, Ti⁴⁺ formed a strong Ti–N chemical bond on the CBN surface, which contributed to improving the wettability and bonding strength between CBN and glass-ceramic bond. After adding TC alloy, the physical properties of the composite were optimized. The porosity, bulk density, flexural strength, Rockwell hardness, CTE, and thermal conductivity of the composites were 5.8%, 3.16 g/cm³, 175 MPa, 90.5 HRC, 3.74 × 10⁻⁶ °C⁻¹, and 5.84 W/(m·k), respectively.

The continuous advancement of technology has led to escalating demands for superior tribological performance in industrial applications, necessitating the enhancement of ceramic materials’ frictional properties through innovative approaches. Solid-lubricant embedding is a widely employed lubrication strategy in metals. However, the challenge of machining holes on ceramic surfaces remains a significant barrier to applying this lubrication technique to ceramics. Gel casting, as a near-net-shaping process, offers several advantages, including uniform green body density, low organic content, and the capability to fabricate components with complex geometries, making it a promising solution for addressing these challenges. In this study, alumina ceramics with small surface holes designed for embedding oil-containing microcapsules were fabricated via gel casting using an N-hydroxy methylacrylamide gel system, which demonstrates lower toxicity compared to conventional acrylamide systems. The fabricated alumina ceramic materials exhibited a high density of 98.2%, a hardness of 16 GPa, and a bending strength of 276 MPa. The oil-containing microcapsules were self-synthesized using hexafluorophosphate ionic liquid as the core material and polyurea-formaldehyde as the wall material. The research results show that under conditions of using an alumina ball, sliding speed of 10 cm/min, load of 5 N, and at room temperature, the material with a microcapsule content of 15 wt% and embedded hole diameter of 1.2 mm reduced the friction coefficient from 0.696 in an unlubricated condition to 0.317. Moreover, the embedding of microcapsules further improved the wear resistance of the alumina.