Chemical co-precipitation from ferrous and ferric salts at a 1:1.9 stoichiometric ratio in NH₄OH base with ultrasonication (sonolysis) in a low vacuum environment has been used for obtaining colloidal suspensions of Fe₃O₄ nanoparticles coated with citric acid. Before coating, the nanoparticles were processed by electrohydraulic discharges with a high discharge current (several tens of amperes) in a water medium using a pulsed direct current. Magnetite nanoparticles were obtained with an average crystallite diameter D = 25–28 nm as obtained by XRD and particle sizes of 25 nm as measured by small-angle X-ray scattering. Magnetometry showed that all samples were superparamagnetic. The saturation magnetization for the citric acid covered samples after electrohydraulic processing showed higher value (58 emu/g) than for the directly coated samples (50 emu/g). Ultraviolet-visible spectroscopy and Fourier transform infrared spectroscopy showed the presence and binding of citric acid to the magnetite surface by chemisorption of carboxylate ions. Hydrodynamic sizes obtained from DLS and zeta potentials were 93 and 115 nm, −26 and −32 mV for the citric acid covered nanoparticles and 226 nm and 21 mV for the bare nanoparticles, respectively. The hydraulic discharge treatment resulted in a higher citric acid coverage and better particle dispersion. The developed method can be used in nanoparticle synthesis for biomedical applications.

In this study, we investigated the cytotoxicity of doxorubicin (DOX)-loaded magnetic nanofluids on 4T1 mouse tumor epithelial cells and MDA-MB-468 human triple-negative breast cancer (TNBC) cells. Superparamagnetic iron oxide nanoparticles were synthesized using sonochemical coprecipitation by applying electrohydraulic discharge treatment (EHD) in an automated chemical reactor, modified with citric acid and loaded with DOX. The resulting magnetic nanofluids exhibited strong magnetic properties and maintained sedimentation stability in physiological pH conditions. The obtained samples were characterized using X-ray diffraction (XRD), transmission electron microscopy (TEM), Fourier-transform infrared spectroscopy, UV-spectrophotometry, dynamic light scattering (DLS), electrophoretic light scattering (ELS), vibrating sample magnetometry (VSM), and transmission electron microscopy (TEM). In vitro studies using the MTT method revealed a synergistic effect of the DOX-loaded citric-acid-modified magnetic nanoparticles on the inhibition of cancer cell growth and proliferation compared to treatment with pure DOX. The combination of the drug and magnetic nanosystem showed promising potential for targeted drug delivery, with the possibility of optimizing the dosage to reduce side-effects and enhance the cytotoxic effect on cancer cells. The nanoparticles’ cytotoxic effects were attributed to the generation of reactive oxygen species and the enhancement of DOX-induced apoptosis. The findings suggest a novel approach for enhancing the therapeutic efficacy of anticancer drugs and reducing their associated side-effects. Overall, the results demonstrate the potential of DOX-loaded citric-acid-modified magnetic nanoparticles as a promising strategy in tumor therapy, and provide insights into their synergistic effects.

The very high capture cross-section of (epi)thermal neutrons by the boron isotope ¹⁰B makes elemental boron and its compounds and composites prospective for serving as materials intensively interacting with neutron irradiation. In their nanostructured form, boron-rich materials reveal properties that improve their radiation-performance characteristics. In this regard, new technologies have been proposed for the synthesis of nanocomposites with matrices of boron carbide B₄C and hexagonal boron nitride h-BN. For the first time, boron carbide-tungsten and hexagonal boron nitride–(iron,magnetite) composites were obtained, respectively, in the form of layered/sandwich structures of components B₄C and W and h-BN nanopowders coated/intercalated with magnetic nanoclusters of iron Fe or magnetite Fe₃O₄. Studying of their chemical/phase composition, structure/morphology, and some other properties leads to the conclusion that the developed B₄C–W and h-BN–(Fe,Fe₃O₄) composites would be useful for solving important problems of boron-based neutron shielding and BNCT (Boron Neutron Capture Therapy), such as attenuating the gamma-radiation accompanying the absorption of neutrons by ¹⁰B nuclei and targeted delivery of ¹⁰B nuclei, as BNCT therapeutic agents, to tumor tissues using control by an external magnetic field, respectively.

Superparamagnetic iron oxide nanoparticles (SPIONs) have attracted the particular interest of scientists from various disciplines since their obtaining to the present day. The physicochemical and pharmacokinetic properties of SPIONs-containing magnetic nanofluids, and their applicability in biomedicine, largely depend on the stability of the colloidal system, particle size, size distribution, net magnetic moment, phase composition, and type and properties of stabilizers. Also, in some cases, when using magnetic nanoparticles for biomedical purposes, it is necessary that the stabilizing ligands of nanoparticles should not significantly change the magnetic properties. From this point of view, the preparation of stable colloidal systems containing bare iron oxide nanoparticles (BIONs) in water at physiological pH attracts particular attention and becomes increasingly popular in scientific circles. This study is focused on the development of the synthesis of aqueous suspensions of SPIONs stabilized with various organic molecules (oleic acid [OA] and poly(ethylene glycol) monooleate - with molecular weights 460 and 860) using a modified controlled chemical coprecipitation reaction, as well as stable nanofluids containing BIONs in an aqueous medium at neutral pH (near-physiological). The obtained samples were characterized using X-ray diffraction (XRD), Fourier Transform Infrared Spectroscopy, small-angle x-ray scattering (SAXS), dynamic light scattering (DLS), electrophoretic light scattering (ELS), and Vibrating Sample Magnetometry.

The rapid progress in nanotechnology has introduced multifunctional iron oxide nanoparticles as promising agents in cancer treatment. This research focused on the synthesis and assessment of citric-acid-coated, folic-acid-conjugated nanoparticles loaded with doxorubicin, evaluating their therapeutic potential in tumor models. An advanced automated continuous technology line (CTL) utilizing a controlled co-precipitation method was employed to produce highly dispersive, multifunctional nanofluids with a narrow size distribution. Various techniques, including dynamic light scattering (DLS), electrophoretic light scattering (ELS), X-ray diffraction (XRD), and transmission electron microscopy (TEM), were employed to examine the particle size, zeta potential, structure, and morphology. Magnetic properties were analyzed through vibrating sample magnetometry (VSM), and surface modifications were confirmed via UV-visible (UV-Vis) and Fourier-Transform Infrared (FTIR) spectroscopy. Cytotoxicity and drug delivery efficiency were evaluated in vitro using RM1 (prostate cancer) and MEC1 (chronic lymphocytic leukemia) cell lines. Fluorescence microscopy demonstrated the successful intracellular delivery of doxorubicin, showcasing the nanoparticles’ potential for targeted cancer therapy. However, folic-acid-conjugated nanoparticles exhibited diminished effectiveness over time. This study highlights the importance of nanoparticle optimization for enhancing therapeutic performance. Further research should aim to improve nanoparticle formulations and explore their long-term impacts for the development of safe, targeted cancer treatments.

Gold nanoparticles mediated tuning of thermo-optical parameters in gold nanoparticles doped cholesteric liquid crystal nanocomposite. / G. Petriashvili, L. Devadze, Ts. Zurabishvili, N. Sepashvili, A. Chirakadze, T. Bukia, J. Markhulia, M. Areshidze, L. Sharashidze, Sh. Akhobadze, E. Arveladze, G. Sanikidze. – 2021–2022. – # 21/22. – pp. 111-124. – Eng. Systems of nanoparticles (NPs) dispersed in liquid crystals (LCs) have attracted attention for the possible development of novel materials based on the controlled assembly of the NPs. There is investigated the formation of free-standing nanocomposites formed by the co-assembly of gold nanoparticles (GNPs) in the cholesteric liquid crystal (CLC) structures. It is found that increasing the concentration of GNPs in the CLC-mixture causes a significant modification of CLC structure and tuning of selective reflection band (SRB) over the optical spectrum. Furthermore, it is demonstrated that a light emission in the luminescent dye-doped CLC/GNPs-nanostructure can be increased dramatically when doped with a certain quantity of GNPs. The pumping laser beam onto the CLC/GNPs-nanostructure causes a temperature increase of this nanocomposite followed by SRB shifting of and spectral tuning of the stimulated laser emission lines from CLC/GNPs-nanocomposite. Fig. 11, Ref. 24.