The CoCrFeNi system is one of the most important high entropy alloys (HEAs) systems. By adding and adjusting the alloy element components and using different synthesis methods, different phases, organization and microstructure can be obtained, thus improving their properties. In this study, CoCrFeNiTi_x HEAs with various Ti contents (x in molar ratio, x = 0, 0.5, 1.0, 1.5) were fabricated by an electrochemical process by virtue of different oxides. The impacts of different Ti contents on the structure, distribution of elements, mechanical properties and corrosion behavior were researched using XRD, EDX and other testing methods. The bulk CoCrFeNiTi_x (x = 0, 0.5, 1.0, 1.5) HEAs could be obtained through vacuum hot pressing sintering process (VHPS), which had a single-phase FCC structure. The results of the study showed that the bulk CoCrFeNiTi_x exhibited superior ultimate tensile strength (UTS) and hardness, with the UTS of CoCrFeNiTi as high as 783 MPa and the hardness of CoCrFeNiTi_1.5 reaching 669 HV. The corrosion behavior of CoCrFeNiTi_x (x = 0, 0.5, 1.0, 1.5) HEAs in 0.5 M H₂SO₄, 1 M KOH and 3.5 wt% NaCl was improved with addition of Ti. CoCrFeNiTi_x (x = 0, 0.5, 1.0, 1.5) HEAs have great potential for application in the fields of biomedical coating and aerospace, as well as extreme military industry, etc.

Cattail-grass-derived porous carbon as high-capacity anode materials were prepared via high-temperature carbonization and activation with KOH. The samples exhibited different structures and morphologies with increasing treatment time. It was found that the cattail grass with activation treatment—1 (CGA-1) sample obtained at 800 °C for 1 h presented excellent electrochemical performance. As an anode material for lithium-ion batteries, CGA-1 showed a high charge–discharge capacity of 814.7 mAh g⁻¹ at the current density of 0.1 A g⁻¹ after 400 cycles, which suggests that it has a great potential for energy storage.

Ultra-high Temperature Oxidation-Resistant Alloys (UTORAs) have received a lot of attention due to the increased research demand for deep space exploration around the world. However, UTORAs have the disadvantages of easy oxidation and chalking. So, in this study, a UTORAs is prepared by hot-press sintering on VZrHfNbTa (HEA: High Entropy Alloys can generally be defined as more than five elements by the equal atomic ratio or close to the equal atomic ratio alloying, the mixing entropy is higher than the melting entropy of the alloy, generally forming a high entropy solid solution phase of a class of alloys.) a substrate coated with hafnium. The bonding mechanism, resistance to high-temperature oxidation, and hardness of the sample tests are carried out. The results show that zirconium in the matrix will diffuse into the hafnium coating during the high-temperature sintering process and form the HfZr alloy transition layer, the coating thickness of the composite is about 120 μm, and the diffusion distance of zirconium in the hafnium coating is about 60 μm, this transition layer chemically combines the hafnium coating and the HEA substrate into a monolithic alloy composite. The results of high-temperature oxidation experiments show that the oxidation degree of the hafnium-coated VZrHfNbTa composite material is significantly lower than that of the VZrHfNbTa HEA after oxidation in air at 1600 °C for 5 h. The weight gain of the coated sample after oxidation is 56.56 mg/cm², which is only 57.7% compared to the weight gain of the uncoated sample (98.09 mg/cm² for uncoated), and the surface of the uncoated HEA shows obvious dents, oxidation, and pulverization occurred on the surface and interior of the sample. In contrast, the coated composite alloy sample mainly undergoes surface oxidation sintering to form a dense HfO₂ protective layer, and the internal oxidation of the hafnium-coated VZrHfNbTa composite alloy is significantly lower than that of the uncoated VZrHfNbTa HEA.