This study aimed to investigate the impact of corrosion on the microstructure and tensile properties of 7075 high-strength alloy. It involved outdoor exposure tests in an actual marine atmospheric environment in Wanning, Hainan Province. The results showed that the 7075 alloy was corroded rapidly in the marine atmospheric environment, and corrosion pits and intergranular cracks were generated. The intergranular cracks were extended along the grain boundary during corrosion, leading to the exfoliation of the matrix. The cause for the intergranular corrosion was discussed based on the microstructure characteristics of 7075 alloy. The tensile properties of the 7075 alloy gradually deteriorated with the increase of exposure time in the marine atmospheric environment. The ultimate strength and elongation were decreased by about 3.2% and 58.3%, respectively, after 12 months of outdoor exposure.

The microstructure and mechanical properties of semi-continuous casting Mg-Gd-Y-Zr magnesium alloys with different Zn contents were studied in this paper. The results showed that an increase in Zn content resulted in gradual refinement of the grains and a gradual increase in the volume fraction of the second phase. At a Zn content of 0.7 wt%, the microstructure was mainly composed of the α-Mg matrix and the Mg5(GdY) and long-period stacking order (LPSO) phases. An increase in the Zn content lowered the volume fraction of the Mg5(GdY) phase and increased the volume fraction of the LPSO phase. At a Zn content of 3.3 wt%, the microstructure was mainly composed of the α-Mg matrix and the LPSO phase. Among these alloys, the alloy without Zn addition showed an optimal ultimate tensile strength and yield strength of 229 MPa and 185 MPa, respectively, while the alloy with 3.3 wt% Zn showed an excellent elongation after fracture of 4.5%. The tensile fracture analysis indicated that the cracks of the alloy without Zn mainly originated at the trigeminal junction of the grain boundary, the cracks of the 0.7 wt% Zn and 1.5 wt% Zn alloy mainly originated at the interface of the Mg/lamellar LPSO phase, and the cracks of the 3.3 wt% Zn alloy mainly originated at the bulk LPSO phase of the grain boundary and then propagated along the bulk LPSO phase.