To expand the application range of fast-growing poplar, a modification method of poplar impregnated with nano-SiO₂ and urea-formaldehyde resin was proposed in this study. Taking the mass ratio of nano-SiO₂ mass to the solid content of urea-formaldehyde resin impregnation solution (W), high-temperature (H), and high-temperature time (T) as influencing factors, the effects of impregnation high-temperature heat treatment modification on the physical and mechanical properties of fast-growing poplar were explored. At the same time, the weight loss rate, oven-dry density, dry shrinkage properties, swelling properties, modulus of rupture (MOR), and modulus of elasticity (MOE) of the modified poplar were measured. The research results show that both the weight loss rate and the coefficient of variation of the oven-dry density have a high correlation with the temperature; the high-temperature immersion heat treatment can reduce the dry shrinkage and swelling of poplar, improve the dimensional stability, MOR, and MOE. W is 0–1%, H is 160 °C, and T is 2–4 h. The impregnated heat-treated wood has good MOR and MOE. Therefore, the combination of nano-SiO₂ and urea-formaldehyde resin impregnation and heat treatment to modify poplar can improve some physical and mechanical properties of fast-growing poplar, expand the use of poplar, increase its added value, and realize high-value utilization.

To promote the performance of fast-growing poplar wood for furniture applications, this study proposes and investigates the feasibility of modifying fast-growing poplar wood with a urea-formaldehyde resin impregnating agent by adding nano-SiO₂ as a way to improve its physical and mechanical properties. By observing the solubility of nano-SiO₂ addition in urea-formaldehyde resin, determine the optimal ratio of nano-SiO₂ addition to the solid content of the urea-formaldehyde resin solution. After the fast-growing poplar specimens were treated with nano-SiO₂/UF resin, the water absorption, wet swelling, dry shrinkage, nail grip, flexural strength, and modulus of flexural elasticity of the fast-growing poplar specimens were compared and analyzed to determine the effect of impregnation modification and the optimal impregnation ratio. The results showed that the physical and mechanical properties of fast-growing poplar wood were significantly improved by impregnating the fast-growing poplar wood with urea-formaldehyde resin with SiO₂, and the impregnation modification was beneficial to reducing the wet swelling and dry shrinkage of poplar wood, increasing its dimensional stability, improve the grip nail strength, and increase the flexural strength and flexural modulus of elasticity with the increase in nano-SiO₂ concentration.