Raman and IR spectroscopy were used to examine polyvinyl alcohol (PVA) thermally treated in air or vacuum. It was found that after several hours of treatment in air at 470 K bands in Raman spectrum disappear. After vacuum treatment some bands disappear and other become stronger, and slightly change their positions. Such a phenomenon is attributed to the increase of molecular polarizability along polymer chain caused by conjugation.

Apatite is widely used in medicine as a biomaterial for bone tissue restoration. Properties of apatite depend on its composition, including the Ca/P ratio. This paper shows what range of Ca/P ratio can be attained in apatite by the mechanochemical method of synthesis, providing fast formation of a single-phase product. The synthesis was carried out from a reaction mixture of CaHPO₄ and CaO at different Ca/P ratios in the range of 1.17–2.10. The products were studied by PXRD, FTIR and NMR spectroscopy, HRTEM, and STA. In mixtures with a low initial Ca/P ratio (1.17–1.48), directly in the mill, the formation of calcium orthophosphate with whitlockite structure containing an HPO₄²⁻ group and structural water is shown for the first time. This phosphate has structure similar to that of whitlockites of hydrothermal origin and differs from high-temperature β-tricalcium phosphate that has composition Ca₃(PO₄)₃. A series of samples of apatite was obtained with varied composition, which depends on the initial Ca/P ratio. At Ca/P < 1.67, the formation of two types of calcium-deficient apatite was documented. At Ca/P > 1.67, the existence of two types of calcium-rich apatite is confirmed.

Highly porous expanded graphite was synthesized by the programmable heating technique using heating with a constant rate (20 °C/min) from room temperature to 400–700 °C. The samples obtained were analyzed by scanning electron microscopy, energy-dispersive spectroscopy, low-temperature nitrogen adsorption, X-ray photoelectron spectroscopy, Raman spectroscopy, thermogravimetry, and differential scanning calorimetry. A comparison between programmable heating and thermal shock as methods of producing expanded graphite showed efficiency of the first one at a temperature 400 °C, and the surface area reached 699 and 184 m²/g, respectively. The proposed technique made it possible to obtain a relatively higher yield of expanded graphite (78–90%) from intercalated graphite. The experiments showed the advantages of programmable heating in terms of its flexibility and the possibility to manage the textural properties, yield, disorder degree, and bulk density of expanded graphite.

Hybrid materials of polyvinyl alcohol-hydroxides/oxides of Be, Mg, Zn, Cd, B, Al, Cr, and Fe have been obtained. The studies have been carried out by the methods of optical spectroscopy, X-ray diffraction, and synchronous thermal analysis. Interpretation of experimental data is presented, presuming that, in systems with zinc, boron, aluminum, chromium, and iron hydroxides/oxides, interpolymeric complexes of polyvinyl alcohol with corresponding polymeric inorganic compounds are formed. They belong to a new class of materials with unusual structure containing chains of inorganic polymers isolated in the organic matrix.

Hydroxyapatite (HA), the major mineral component of tooth enamel and natural bones, is a good candidate for bone tissue engineering. Synthetic HA is used for making coatings on metallic implants intended for medical applications. A HA coating renders the implant biocompatible and osteoinductive. In addition, it improves fixation and the overall performance of the implanted object. In the present work, HA coatings were deposited on a medical titanium alloy implant with mesh geometry and a developed surface by detonation spraying. The feedstock powder was HA obtained by the dry mechanochemical method. Single-phase HA coatings were obtained. The coatings were formed not only on the surfaces normal to the particle flow direction, but also on the sides of the mesh elements. Despite partial melting of the powder, no decomposition of HA occurred. This work demonstrates the prospects of detonation spraying for the production of HA coatings on metallic implants with complex geometries.